1、362010年第25卷第12期CHINA COATINGS 技术研发T echnical Research and Development高耐候水性氟碳铝粉涂料的研制Preparation of High-weatherability Water-borne Fluorocarbon Aluminum Powder Coatings 赵兴顺,赵洪良,李缙成,刘洪珠,高 达(大连振邦氟涂料股份有限公司,辽宁大连 116036Zhao Xingshun, Zhao Hongliang, Li Jincheng, Liu Hongzhu, Gao Da(Dalian Zebon Fluorocarb

2、on Coatings Co., Ltd., Dalian 116036, Liaoning ProvinceAbstract:Selecting high quality water-borne aluminum paste, high efficiency dispersant, high-weatherability water-borne uorocarbon resin and suitable anti-aging agent, we have prepared water-borne uorocarbon aluminum powder coatings with the art

3、i cial aging performance of 5000h.Keywords:high-weatherability, water-borne, uorocarbon coatings, aluminum powder coatings, metal coatings摘要:通过选择优质水性铝浆、高效分散剂、高耐候水性氟树脂和适宜抗老化助剂,研制出耐人工老化高达5 000 h以上的水性氟碳铝粉涂料。关键词:高耐候;水性;氟涂料;铝粉涂料;金属涂料中图分类号:TQ630.7 文献标识码:A 文章编号:1006-2556(201012-0036-030 前 言溶剂型仿铝塑板氟碳金属涂料,具有

4、耐腐蚀、耐盐雾、耐酸雨、耐各种复杂环境、使用期限长、逼真的扣板效果以及造价低、施工简便等优点,越来越多地被建筑外墙高档装饰工程所采用。但在实际应用过程中,溶剂型仿铝塑板氟碳金属涂料存在涂膜透气性差、溶剂易渗透到基材损坏保温板、需要清漆罩面等缺点,涂层易起皮、剥落。水性氟碳铝粉涂料安全、环保、透气性佳,同时具有良好的耐候性、耐沾污性和耐化学品性以及造价更低、施工更方便等特点,成为高档外墙涂料重要品种,逐步得到市场的认可。目前水性氟碳铝粉涂料的耐人工加速老化一般在3 000 h左右,无法满足市场对更高性能涂料的要求。本研究主要从优质水性铝浆的选择、高效分散剂的选择、高耐候水性氟树脂的选择和适宜抗老化助剂的选择等4个方面,提高水性氟碳铝粉涂料的耐老化性能,研制高耐候的水性氟碳铝粉涂料。1 试验部分1.1 主要原材料水性氟树脂:自制;水性铝浆:爱卡、新博来、东洋、舒伦克、崇明、族兴、金阳洋等;其他助剂均为市售。1.2 涂料配方及制造水性氟碳铝粉涂料的配方见表1。制备工艺如下:(1先将水、润湿分散剂、助溶剂、消泡剂、抗氧化剂、防腐剂预混合,加入水性铝浆,中速搅拌1520 min,分散均匀,制成铝浆水溶液。(2在乳液中加入成膜助剂,搅拌均匀,然后缓慢加入