表2板材的温室力学性能,,,,,,
牌号,状态,厚度/mm,抗拉强度R/Mpa,规定非比列延伸强度R0.2/Mpa,断后伸长率A/%,
TA1ELI,M,0.3~25.0,≥200,≥140,≥30,
TA1,M,0.3~25.0,≥240,≥170,≥25,
TA2,M,0.3~25.0,≥400,≥275,≥25,
TA3,M,0.3~25.0,≥500,≥380,≥20,
TA4,M,0.3~25.0,≥580,≥485,≥20,
TC4,M,0.8~4.75,≥925,≥870,≥10,
,,>4.75~25.0,≥895,≥830,≥10,
TC4ELI,M,0.8~25.0,≥860,≥795,≥10,
a厚度小于0.64mm的纯钛和厚度不大于1.60mm的板材,断后伸长率报实测值。,,,,,,
表3板材的弯芯直径和弯曲角,,,,,,
牌号,状态,弯芯直径,,弯曲角α/(°),,
,,板材名义厚度T/mm,,,,
,,≤2.0(钛合金<1.8),>2.0~5.0(钛合金1.8~4.75),,,
TA1ELI,M,3T,4T,105,,
TA1,M,3T,4T,105,,
TA2,M,4T,5T,105,,
TA3,M,4T,5T,105,,
TA4,M,5T,6T,105,,
TC4,M,9T,10T,105,,
TC4ELI,M,9T,10T,105,,
表4棒材温室力学性能,,,,,,
牌号,状态,直径或边长/mm,抗拉强度R/Mpa,规定非比列延伸强度R/Mpa,断后伸长率A/%,断面收缩率Z/%
TA1ELI,M,>7~90,≥200,≥140,≥30,≥30
TA1,M,,≥240,≥170,≥24,≥30
TA2,M,,≥400,≥275,≥20,≥30
TA3,M,,≥500,≥380,≥18,≥30
TA4,M,,≥580,≥485,≥15,≥25
TC4,M,>7~50,≥930,≥860,≥10,≥25
,M,>50~90,≥895,≥830,≥10,≥25
TC4ELI,M,>7~45,≥860,≥795,≥10,≥25
,M,>45~65,≥825,≥760,≥8,≥20
,M,>65~90,≥825,≥760,≥8,≥15
TC20,M,>7~100,≥900,≥800,≥10,≥25
注:直径大于75mm的棒材取棒向试样。,,,,,,
表5丝材的室温性能,,,,,,
牌号,状态,直径/mm,温室力学性能,,,
,,,R/Mpa,A/%,,
TA1ELI,M,3.2~7.0,≥200,≥30,,
TA1,M,,≥240,≥24,,
TA2,M,,≥400,≥20,,
TA3,M,,≥500,≥18,,
TA4,M,,≥580,≥15,,
TA1ELI,M,0.5~<3.2,≥200,≥18,,
TA1,M,,≥240,≥15,,
TA2,M,,≥400,≥12,,
TA3,M,,≥500,≥10,,
TA4,M,,≥580,≥8,,
TC4,M,1.0~2.0,≥925,≥8,,
,M,≥2.0~7.0,≥895,≥10,,
TC4ELI,M,1.0~7.0,≥860,≥10,,
TC20,M,1.0~7.0,≥900,≥10,,
a是直径小于1.60的丝材的断后延长率A报实测值。,,,,,,
表2,,,,,,
牌号,温室力学性能,不小于,,,,,
,抗拉强度R/Mpa,规定非比列延伸强度R/Mpa,断后伸长率A/%,断面收缩率Z/%,备注,
TA1,240,140,24,30,,
TA2,400,275,20,30,,
TA3,500,380,18,30,,
TA4,580,485,15,25,,
TA5,685,585,15,40,,
TA6,685,585,10,27,,
TA7,785,680,10,25,,
TA9,370,250,20,25,,
TA10,485,345,18,25,,
TA13,540,400,16,35,,
TA15,885,825,8,20,,
TA19,895,825,10,25,,
TB2,≤980,820,18,40,淬火性能,
,1370,1100,7,10,时效性能,
TC1,585,460,15,30,,
TC2,685,560,12,30,,
TC3,800,700,10,25,,
TC4,895,825,10,25,,
TC4ELI,830,760,10,15,,
TC6,980,840,10,25,,
TC9,1060,910,9,25,,
TC10,1030,900,12,25,,
TC11,1030,900,10,30,,
TC12,1150,1000,10,25,,
aTC6棒材测定普通退货状态的性能。当需方要求并在合同中注明时,方测定等温退火状态的性能。,,,,,,
表3,,,,,,
牌号,试验温度/℃,高温力学性能,不小于,,,,
,,抗拉强度R/Mpa,持久强度/Mpa,,,
,,,100h,50h,35h,
TA6,350,420,390,—,—,
TA7,350,490,440,—,—,
TA15,500,570,—,470,—,
TA19,480,620,—,—,480,
TC1,350,345,325,—,—,
TC2,350,420,390,—,—,
TC4,400,620,570,—,—,
TC6,400,735,665,—,—,
TC9,500,785,590,—,—,
TC10,400,835,785,—,—,
TC11,500,685,—,—,640,
TC12,500,700,590,—,—,
aTC11钛合金棒材持久强度不合格时,允许再按500℃的100h持久强度100h≥590MPa进行检验,检验合格则该批棒材的持久强度合格。,,,,,,
表4,,,,,,
直径或截面厚度,允许偏差,,,,,
,热锻造或挤压棒,热轧棒,车(磨)光棒、冷轧或冷拉棒,,,
>7~15,±1.0,0.6,±0.3,,,
,,0.5,,,,
>15~25,±1.5,0.7,±0.4,,,
,,0.5,,,,
>25~40,±2.0,1.2,±0.5,,,
,,0.5,,,,
>40~60,±2.5,1.5,±0.6,,,
,,1,,,,
温馨提示
- 1. 本站所有资源如无特殊说明,都需要本地电脑安装OFFICE2007和PDF阅读器。图纸软件为CAD,CAXA,PROE,UG,SolidWorks等.压缩文件请下载最新的WinRAR软件解压。
- 2. 本站的文档不包含任何第三方提供的附件图纸等,如果需要附件,请联系上传者。文件的所有权益归上传用户所有。
- 3. 本站RAR压缩包中若带图纸,网页内容里面会有图纸预览,若没有图纸预览就没有图纸。
- 4. 未经权益所有人同意不得将文件中的内容挪作商业或盈利用途。
- 5. 人人文库网仅提供信息存储空间,仅对用户上传内容的表现方式做保护处理,对用户上传分享的文档内容本身不做任何修改或编辑,并不能对任何下载内容负责。
- 6. 下载文件中如有侵权或不适当内容,请与我们联系,我们立即纠正。
- 7. 本站不保证下载资源的准确性、安全性和完整性, 同时也不承担用户因使用这些下载资源对自己和他人造成任何形式的伤害或损失。
最新文档
- 2023年教科版四年级科学上册单元复习资料全册
- 2024至2030年中国亚硝酸钡行业发展预测及投资策略报告
- 2024至2030年中国单座调节阀市场前景及投资发展战略研究报告
- 建筑工地安全防护设施检查考核试卷
- 搪瓷制品的生产设备选型与维护管理考核试卷
- 环境保护行动计划与实施考核试卷
- 有关销售实习报告范文汇编9篇
- 混血豺王读后感3篇
- 主题班会通知
- 2024年增采原油起振机项目合作计划书
- 动火作业危害分析(JHA)评价表
- 《发展投掷能力的练习与游戏》教学设计
- EMR内镜下黏膜切除术
- 担保机构资本金托管协议
- 煤矿安全生产法律法规
- 部编版五年级上册语文第一单元复习《单元测试》03及答案
- 汽车专业介绍
- 聚氨酯防水涂料施工方案
- 绩效评价报告样板(粮食储备补贴)
- 2023版思想道德与法治专题二领悟人生真谛课件
- 11《个人信用报告异议申请表》
评论
0/150
提交评论