焊接工艺评定报告(PQR1-15)

焊接工艺评定报告(PQR1-15)2 PWHT材料标准GB713W.M.Standard钢号Q345RSteedBrand类、组别号Fe-1-2与类、组别号Fe-1-2相焊Category.AssemblyNo.WithCategory.AssemblyNo.Welding厚度12mmThickness直径/Diameter其他/Others温温度范围(℃)/TemperatureRegion保温时间(h)/TimeHold保护气体：ShieldingGas气体种类混合比流量(L/min)GasCategocyMixtureFlowRate保护气Ar99.9910 SG尾保气///TSG背保气///焊焊材标准W.M.StandardNB/T47018.3/NB/T47018.2焊材牌号W.M.BrandER50-6/J506焊材规格WeldingSpecificationØ2.5/.缝0金属厚度WeldMetalThickness12mm其他Others/电电流种类WeldingCurrent(A)直流(DC)极性Polarity正接(EN)反接(EP)钨极尺寸TungstenElectrodeSize2.5焊接电流(A)WeldingCurrent(A)120/160/140/140电弧电压(V)ArcVotage(V)13/26/24/24其他Others/焊材牌号/BendingTest号:TensionTestReportNo焊材牌号/BendingTest号:TensionTestReportNo.PQR16-01HP试样对接焊缝位置平焊方向(向上、向下)PositionOfButtWeldFlatnessDirection(Upward,Downward)角焊缝位置/方向(向上、向下)PositionOfFilletWeldDirection(Upward,Down技术措施Technicalmeasur焊接速度(cm/min)12/16/13/13WeldingSpeed摆动焊或不摆动焊/WeaveBeadWeldingOrNonweaveBeadWelding摆动参数/WeaveBeadParameter单道焊或多道焊多道焊SinglePassWeldingOrMulti-passWelding单丝焊或多丝焊单丝焊SingleWireWeldingOrMultiWireWelding/Chemical/ChemicalCompositionOf预热温度(℃)20℃(室温)PreheatingT层间温度(℃)250℃InterpassT其他/OthersCorrosionCorrosionResistantOverlayWeldMetal(%)BrandW.M.BrandCPSH10MnSi0.7340.60.20.9/10.8580.90.30.90.0/拉伸试验TensionTest试验报告编号：拉伸试验TensionTest试验报告编号：TensionTestReportNo.PQR16-01HP试样编号SpecimenNo.试样宽度(mm)SpecimenWidth试样厚度(mm)SpecimenThickness横截面积(mm2)CrossSectionalArea断裂载荷(KN)FractureLoad抗拉强度(Mpa)TensileStrength断裂部位和特征FractureLocationAndBreakPerformance16-01HPL116-01HPL2编号Specimen型Specimen (mm)SpecimenThickness (mm)CenterOfBendD.径(°)AngleOf试验结果TestResultAcceptable弯曲试验试验报告编弯曲试验3硬度检验硬度检验试验报告编号：No.ShapeBend16-01HPM140180°16-01HPM240180°16-01HPB140180°16-01HPB40180°TensionTestReportNo./试样编号SpecimenNoSpecimenDimension缺口类型NotchShape缺口位置NotchCocation冲击温度(℃)ImpactTemp冲击吸收功(J)ce备注Remarks/////////////根部:(焊透、未焊透)焊透根部:(焊透、未焊透)焊透焊缝:Weld:(Fusion、LackOfFusion)Weld、HeatAffectedZone:(Crack、FreeOfCrack)IfardnessIfardnessTestTensionTestReportNo./试样编号SpecimenNopecimenDimension母材硬度值HBBaseMetalHardnessValue焊缝硬度值HBWeldHardnessValueHB热影响区硬度值HBHAZHardnessValueHBTestResultAcceptable无损检验：NDEExaminationRTNB/无损检验：NDEExaminationRTNB/T47013.2-2015100%II级合格UTMT/PT/结论：本评定按NB/T47014-2011规定焊接试件、检验试样、测定性能、确认试验记录正确ofweldingspecimen,performanceofspecimen,examinationandtestingrecord合格焊工姓名Welder焊工代号Welder’sionion2245PWHTPWHT焊材规格WeldingSpecificationØ2.0tal温度范围(℃)焊材标准W.M.Standard电流种类WeldingPrepardeBy&DateviewedByviewedBy&DateAppdBy&AppdBy&Date05验验BaseMetal材料标准GB24511W.M.Standard钢号06Cr19Ni10SteedBrandBaseMetal材料标准GB24511W.M.Standard钢号06Cr19Ni10SteedBrand类、组别号Fe-8-1与类、组别号Fe-8-1相焊Category.AssemblyNo.WithCategory.AssemblyNo.Welding厚度8mmThickness直径/Diameter其他/Others/TemperatureRegion保温时间(h)/TimeHold保护气体：ShieldingGas气体种类混合比流量(L/min)GasCategocyMixtureFlowRate保护气Ar99.9910 SG尾保气///TSG背保气///BSNB/T47018.3焊材牌号W.M.BrandH08Cr21Ni10SiCurrent(A)直流(DC)极性Polarity正接(EN)钨极尺寸TungstenElectrodeSize2.5焊接电流(A)Welding6No.度(mm)Width度(mm)cknNo.度(mm)Width度(mm)ckn荷(KN)actusilFracture其他Others/Current(A)120--180电弧电压(V)ArcVotage(V)14--16其他Others/方向(向上、向下)PositionOfButtWeldssDirectionUpwardDownward)角焊缝位置向方向(向上、向下)PositionOfFilletWeld技术措施Technicalmeasur焊接速度技术措施Technicalmeasur焊接速度(cm/min)8-12WeldingSpeed不摆动weaveBeadWelding/WeaveBeadParameter道焊多道焊SinglePassWeldingOrMulti-passWeldingSingleWireWeldingOrMultiWireWelding其他OthersPreheating预热温度(℃)20Preheating预热温度(℃)20PreheatingT层间温度(℃)sT/焊材牌号/ChemicalCompositionOf焊材牌号/ChemicalCompositionOfBrandW.M.BrandCPSH08Cr21Ni10Si0.3280.11972/TensionTestReportNo.SectionalAreaLocationAndBreakPerformance25.2246.96169582硬度检验试验报告编号：硬度检验试验报告编号：试样号:TensionTestReport试样nNo.试样厚度 (mm)SpecimenThickness弯心直径 (mm)CenterOfBendD.AngleAnglend试验结果TestResultAcceptable16-02HPM14016-02HPB40180°TensionTestReportNo./试样编号SpecimenNoSpecimenDimension缺口类型NotchShape缺口位置NotchCocation冲击温度(℃)ImpactTemp收功ce备注Remarks//////////////////////根部:(焊透、未焊透)根部:(焊透、未焊透)焊透焊缝:Weld:(Fusion、LackOfFusion)Weld、HeatAffectedZone:(Crack、FreeOfCrack)IfardnessIfardnessTestTensionTestReportNo.试样编号SpecimenNopecimenDimension母材硬度值HBBaseMetalHardnessValueWWeldHardnessValueHB热影响区硬度值HBHAZHardnessValueHBTestResultAcceptable无损检验：NDEExaminationRT无裂纹无损检验：NDEExaminationRT无裂纹UTMT/PT/结论：本评定按NB/T47013.2-2015规定焊接试件、检验试样、测定性能、确认试验记录正确ofweldingspecimen,performanceofspecimen,examinationandtestingrecord合格78WelderWelder’sWelder’sYGWeldingn施Weldingn22/Preparde/PrepardeBy&Date/viewed/viewedBy&Date/&Date/&DateAppdBy05NB/T47014-2011焊接工艺评定报告(PQR)单位名称：Fabricator:焊接工艺评定报告编号PQR16-03HP预焊接工艺规程编号pWPS16-03HPWPSNoPQRNo焊接方法钨极氩弧焊打底/焊条电弧焊盖面机械化程度(手工、半自动、自动)手工BaseMetal材料标准BaseMetal材料标准GB713、GB511W.M.Standard号H12Cr24Ni13/A302PWHT温度范围(℃PWHT温度范围(℃)TemperatureRegion保温时间(h)TimeHold保护气体：ShieldingGas气体种类混合比流量(L/min)GasCategocyMixtureFlowRateAr10 SG尾保气///TSG背保气///BSteedBrandteedBrandCategory.AssemblyNo.WithCategory.AssemblyNo.WeldingmmThickness/Diameter/9焊材牌号/焊材牌号/焊材标准W.M.StandardNB/T47018.3焊材牌号W.M.BrandH12Cr24Ni13/A302焊材规格WeldingSpecificationØ2.0/Ø3.2焊缝金属厚度WeldMetalThickness8mm其他Others/电特性ElectricPower电流种类WeldingCurrent(A)直流(DC)极性Polarity反接(EP)钨极尺寸TungstenElectrodeSize2.5焊接电流(A)WeldingCurrent(A)110--160电弧电压(V)ArcVotage(V)24--26其他Others技术技术措施Technical方向(向上、向下)PositionOfButtWeldFlatnessDirection(Upward,Downward)角焊缝位置向方向(向上、向下)PositionOfFilletWeldPreheatingDirection(Upward,DownPreheatingmeameasur焊接速度(cm/min)8-12WeldingSpeed摆动焊或不摆动焊不摆动WeaveBeadWeldingOrNonweaveBeadWelding摆动参数/WeaveBeadParameter单道焊或多道焊多道焊+单道焊SinglePassWeldingOrMulti-passWelding单丝焊或多丝焊单丝焊SingleWireWeldingOrMultiWireWelding/Chemical/ChemicalCompositionOf预热温度(℃)20Preheating预热温度(℃)20PreheatingT层间温度(℃)sT其他CorrosionCorrosionResistantOverlayWeldMetal(%)BrandW.M.BrandCPSH12Cr24Ni13284623A3020.71.130.32371240.4TensionTestReportNo.试验报告编号：pWPS16-03HP弯曲试验试验报告编硬度检验试验报告编号：弯曲试验试验报告编硬度检验试验报告编号：编号SpecimenNo.试样宽度(mm)SpecimenWidth试样厚度(mm)SpecimenThickness横截面积(mm2)CrossSectionalArea荷(KN)FractureLoad抗拉强度(Mpa)TensileStrength断裂部位和特征FractureLocationAndBreakPerformanc25.2230.56162562BendingBendingTest号:TensionTest号:TensionTestReportNo.pWPS16-03HP编号SpecimenNo.试样类型SpecimenShape试样厚度 (mm)SpecimenThickness弯心直径 (mm)CenterOfBendD.弯心直径(°)AngleOfBend试验结果TestResultAcceptable16-03HPM140180°16-03HPB40180°TensionTestReportNo./试样编号SpecimenNoSpecimenDimension缺口类型NotchShape缺口位置NotchCocation冲击温度(℃)ImpactTemp收功ce备注Remarks//////////////////////根部:(焊透、未焊透)焊透根部:(焊透、未焊透)焊透焊缝:Weld:(Fusion、LackOfFusion)Weld、HeatAffectedZone:(Crack、FreeOfCrack)IfardnessIfardnessTestTensionTestReportNo./试样编号SpecimenNopecimenDimension母材硬度值HBBaseMetalHardnessValue焊缝硬度值HBWeldHardnessValueHB热影响区硬度值HBHAZHardnessValueHBTestResultAcceptable无损检验：NDERT无裂纹UT/MT/PT/其他/结论：本评定按NB/T47013.2-2015规定焊接试件、检验试样、测定性能、确认试验记录正确Result:ThisassessmenthasbeenassessedandconformedtoNB/T47014-2011standardrequilementsforpreparationofweldingspecimen,performanceofspecimen,examinationandtestingrecord评定结果合格WelderWelderWelder’sWelder’sYGionionWelding22PrepardeBy&PrepardeBy&DateviewedByviewedBy&DateAppdBy&AppdBy&Date05NB/T47014-2011焊接工艺评定报告(PQR)单位名称：Fabricator:焊接工艺评定报告编号PQR16-04HP预焊接工艺规程编号pWPS16-04HPWPSNoPQRNo焊接方法钨极氩弧焊(GTAW)机械化程度(手工、半自动、自动)手工BaseBaseMetal材料标准GB9948/W.M.Standard20/Q345RSteedBrand类、组别号Fe-1-1与类、组别号Fe-1-2相焊Category.AssemblyNo.WithCategory.AssemblyNo.WeldingPWHT温度范围(PWHT温度范围(℃)TemperatureRegion保温时间(h)TimeHold保护气体：ShieldingGas气体种类混合比流量(L/min)GasCategocyMixtureFlowRate焊材牌号厚焊材牌号Thickness直径Ø19Diameter其他/Others SG尾保气///TSG背保气///BS焊材标准W.M.StandardNB/T47018.3焊材牌号W.M.BrandH10MnSi焊材规格WeldingSpecificationØ2.5焊缝金属厚度WeldMetalThickness≥2mm其他Others/电电流种类WeldingCurrent(A)直流(DC)极性Polarity正接(EN)钨极尺寸TungstenElectrodeSize2.5焊接电流(A)WeldingCurrent(A)120--180电弧电压(V)ArcVotage(V)14--16其他Others技术技术措施Technical方向(向上、向下)PositionOfButtWeldFlatnessDirection(Upward,Downward)角焊缝位置向方向(向上、向下)PositionOfFilletWeldPreheatingDirection(Upward,DownPreheatingmeameasur焊接速度(cm/min)8-12WeldingSpeed摆动焊或不摆动焊不摆动WeaveBeadWeldingOrNonweaveBeadWelding摆动参数/WeaveBeadParameter单道焊或多道焊多道焊SinglePassWeldingOrMulti-passWelding单丝焊或多丝焊单丝焊SingleWireWeldingOrMultiWireWelding/Chemical/ChemicalCompositionOfPreheatingT层间温度(℃)sT/CorrosionCorrosionResistantOverlayWeldMetal(%)BrandW.M.BrandCPSH10MnSi0.7340.60.20.9/1/No.度(mm)Width度(mm)ckn荷(KN)actusilNo.度(mm)Width度(mm)ckn荷(KN)actusilFractureBendingTest号:TensionTestReportNo./根部:(焊透、未焊透)焊透焊缝:Weld:(Fusion、LackOfFusion)Weld、HeatAffectedZone:(Crack、FreeOfCrack)硬度检验试样IfardnessTestTensionTestReportNo.//////试验报告编号：NB/T47014-2011//SectionalAreaLocationAndBreakPerformance///////编号SpecimenNo./型SpecimenShape/试样厚度 (mm)SpecimenThickness/弯心直径 (mm)CenterOfBendD./径(°)AngleOfBend/试验结果TestResultAcceptable/ImpactTestTensionTestReportNo./试样编号SpecimenNo/SpecimenDimension/缺口类型NotchShape/缺口位置NotchCocation/冲击温度(℃)ImpactTemp/冲击吸收功(J)ImpactForce/备注Remarks//试样编号SpecimenNopecimenDimension母材硬度值HBBaseMetalHardnessValue焊缝硬度值HBWeldHardnessValueHB热影响区硬度值HBHAZHardnessValueHBTestResultAcceptable////////////TensionTestReportNo.///////弯曲试验试验报告编弯曲试验无损检验：NDERT/UT/MT/PT/其他/结论：本评定按/规定焊接试件、检验试样、测定性能、确认试验记录正确Result:ThisassessmenthasbeenassessedandconformedtoNB/T47014-2011standardrequilementsforpreparationofweldingspecimen,performanceofspecimen,examinationandtestingrecord评定结果合格WelderWelderWelder’sWelder’sionionWelding22PrepardeBy&PrepardeBy&DateviewedByviewedBy&DateAppdBy&AppdBy&Date05NB/T47014-2011焊接工艺评定报告(PQR)单位名称：Fabricator:焊接工艺评定报告编号PQR16-05HP预焊接工艺规程编号pWPS16-05HPWPSNoPQRNo焊接方法钨极氩弧焊(GTAW)机械化程度(手工、半自动、自动)手工BaseMetal材料标准GB9948/BaseMetal材料标准GB9948/GB511W.M.Standard20/CrNi0teedBrandCategory.AssemblyNo.WithCategory.AssemblyNo.PWHT温度范围(PWHT温度范围(℃)TemperatureRegion保温时间(h)TimeHold保护气体：ShieldingGas气体种类混合比流量(L/min)GasCategocyMixtureFlowRate焊材牌号焊材牌号/厚度30/2.0mmThickness直径Ø19Diameter其他/Others保护气99.9910 SG尾保气///TSG背保气///BS焊材标准W.M.StandardNB/T47018.3焊材牌号W.M.BrandH12Cr24Ni13焊材规格WeldingSpecificationØ2.0焊缝金属厚度WeldMetalThickness≥2mm其他Others/电电流种类WeldingCurrent(A)直流(DC)极性Polarity正接(EN)钨极尺寸TungstenElectrodeSize2.5焊接电流(A)WeldingCurrent(A)120--180电弧电压(V)ArcVotage(V)14--16其他Others技术技术措施Technical方向(向上、向下)PositionOfButtWeldFlatnessDirection(Upward,Downward)角焊缝位置向方向(向上、向下)PositionOfFilletWeldPreheatingDirection(Upward,DownPreheatingmeameasur焊接速度(cm/min)8-12WeldingSpeed摆动焊或不摆动焊不摆动WeaveBeadWeldingOrNonweaveBeadWelding摆动参数/WeaveBeadParameter单道焊或多道焊多道焊SinglePassWeldingOrMulti-passWelding单丝焊或多丝焊单丝焊SingleWireWeldingOrMultiWireWelding/Chemical/ChemicalCompositionOfPreheatingT层间温度(℃)sT/CorrosionCorrosionResistantOverlayWeldMetal(%)BrandW.M.BrandCPSH12Cr24Ni13284623No.度(mm)Width度(mm)ckn荷(KN)actusilNo.度(mm)Width度(mm)ckn荷(KN)actusilFractureBendingTest号:TensionTestReportNo./根部:(焊透、未焊透)焊透焊缝:Weld:(Fusion、LackOfFusion)Weld、HeatAffectedZone:(Crack、FreeOfCrack)硬度检验试样IfardnessTestTensionTestReportNo.试验报告编号：//////NB/T47014-2011//SectionalAreaLocationAndBreakPerformance///////编号SpecimenNo./型SpecimenShape/试样厚度 (mm)SpecimenThickness/弯心直径 (mm)CenterOfBendD./弯心直径(°)AngleOfBend/试验结果TestResultAcceptable/ImpactTestTensionTestReportNo./试样编号SpecimenNo/SpecimenDimension/缺口类型NotchShape/缺口位置NotchCocation/冲击温度(℃)ImpactTemp/冲击吸收功(J)ImpactForce/备注Remarks//试样编号SpecimenNopecimenDimension母材硬度值HBBaseMetalHardnessValue焊缝硬度值HBWeldHardnessValueHB热影响区硬度值HBHAZHardnessValueHBTestResultAcceptableTensionTestReportNo.///////弯曲试验试验报告编弯曲试验/无损检验：N无损检验：NDEExamination//////////RT/UTMTRT/UTMT/PT/结论：本评定按/规定焊接试件、检验试样、测定性能、确认试验记录正确ofweldingspecimen,performanceofspecimen,examinationandtestingrecord合格WelderWelderWelder’sWelder’sionion22PrepardeBy&PrepardeBy&DateviewedByviewedBy&DateAppdBy&AppdBy&Date05NB/T47014-2011焊接工艺评定报告(PQR)单位名称：Fabricator:焊接工艺评定报告编号PQR16-06HP预焊接工艺规程编号pWPS16-06HPWPSNoPQRNo焊接方法钨极氩弧焊(GTAW)机械化程度(手工、半自动、自动)手工母材BaseMetal材料标准W.M.StandardW.M.Standard焊后热处理PWHT温度范围(℃)/TemperatureRegion保温时间(h)/TimeHold保护气体：ShieldingGas气体种类混合比流量(L/min)GasCategocyMixtureFlowRate保护气Ar99.9910 SG尾保气///TSG背保气///06Cr19Ni10/CrNi006Cr19Ni10/CrNi0teedBrandCategory.AssemblyNo.WithCategory.AssemblyNo.WeldingThicknessØ19Diameter/焊NB/T47018.3焊材牌号W.M.BrandH08Cr21Ni10Si焊材规格WeldingSpecificationØ2.0焊缝金属厚度WeldMetalThickness≥2mm其他Others/电电流种类WeldingCurrent(A)直流(DC)极性Polarity正接(EN)钨极尺寸TungstenElectrodeSize2.5焊接电流(A)WeldingCurrent(A)120--180电弧电压(V)ArcVotage(V)14--16其他Others技术技术措施Technical方向(向上、向下)PositionOfButtWeldFlatnessDirection(Upward,Downward)角焊缝位置向方向(向上、向下)PositionOfFilletWeldPreheatingDirection(Upward,DownPreheatingmeameasur焊接速度(cm/min)8-12WeldingSpeed摆动焊或不摆动焊不摆动WeaveBeadWeldingOrNonweaveBeadWelding摆动参数/WeaveBeadParameter单道焊或多道焊多道焊SinglePassWeldingOrMulti-passWelding单丝焊或多丝焊单丝焊SingleWireWeldingOrMultiWireWelding℃℃PreheatingT层间温度(℃)sT//BendingTestMetallographicExamination试样TensionTestReportNo.///////其他Others/ChemicalChemicalCompositionOfCorrosionResistantOverlayWeldMetal(%)W.M.焊材牌号焊材牌号CPSH08Cr21Ni10Si0.3280.11972NBT14-2011焊接工艺评定报告(PQR)//NBT14-2011焊接工艺评定报告(PQR)//号:TensionTestReportNo./拉伸试验TensionTestTensionTestReportNo./试验报告编号：试样编号SpecimenNo.试样宽度(mm)SpecimenWidth试样厚度(mm)SpecimenThickness横截面积(mm2)CrossSectionalArea断裂载荷(KN)FractureLoad抗拉强度(Mpa)TensileStrength断裂部位和特征FractureLocationAndBreakPerformance编号SpecimenNo.型SpecimenShape试样厚度 (mm)SpecimenThickness弯心直径 (mm)CenterOfBendD.弯心直径(°)AngleOfBend试验结果TestResultAcceptable///////试样编号SpecimenNoSpecimenDimension缺口类型NotchShape缺口位置NotchCocation冲击温度(℃)ImpactTemp冲击吸收功(J)ce备注Remarks//////////////试验报告编弯曲试验//////根部:(焊透、未焊透)根部:(焊透、未焊透)焊透焊缝:Root:(Penetration、LackofPenetration)Weld:(Fusion、LackOfFusion)焊缝、热影响区：(有裂纹、无裂纹)无裂纹硬度检验试验报告编号：Weld、HeatAffectedZone:(Crack、FreeOf硬度检验试验报告编号：IfardnessIfardnessTestTensionTestReportNo./试样编号SpecimenNopecimenDimension母材硬度值HBBaseMetalHardnessValue焊缝硬度值HBWeldHardnessValueHB热影响区硬度值HBHAZHardnessValueHBTestResultAcceptable无损检验：NDEExaminationRT/无损检验：NDEExaminationRT/UTMT/PT/结论：本评定按/规定焊接试件、检验试样、测定性能、确认试验记录正确ofweldingspecimen,performanceofspecimen,examinationandtestingrecord合格WelderWelderWelder’sWelder’sionion22PrepardeBy&PrepardeBy&DateviewedByviewedBy&DateAppdBy&AppdBy&Date05NB/T47014-2011焊接工艺评定报告(PQR)单位名称：Fabricator:焊接工艺评定报告编号PQR16-07HP预焊接工艺规程编号pWPS16-07HPWPSNoPQRNo焊接方法焊条电弧焊(SMAW)机械化程度(手工、半自动、自动)手工WeldingMethodExtentofmechanization(Manual、SemiAuto、Automation)BaseMetal材料标准GB9948/W.M.Standard钢号20/Q345RSteedBrand类、组别号Fe-1-1与类、组别号Fe-1-2相焊Category.AssemblyNo.WithCategory.AssemblyNo.Welding厚度12/3.0mmThickness直径Ø57Diameter其他/OthersPWHT温度范围(℃)TemperaturePWHT温度范围(℃)TemperatureRegion保温时间(h)TimeHold保护气体：ShieldingGas气体种类混合比流量(L/min)GasCategocyMixtureFlowRate/TSGSpecificationØ3.2/Ø4.0SpecificationØ3.2/Ø4.0tal其他Others焊材标准W.M.StandardNB/T47018焊材牌号W.M.Brand焊材规焊材规格WeldingBS电特性ElectricPower电BS电特性ElectricPowerCurrent(A)直流(DC)极性Polarity反接(EP)钨极尺寸TungstenElectrodeSize/焊接电流(A)WeldingCurrent(A)120--180电弧电压(V)ArcVotage(V)14--16其他Others技术技术措施Technical方向(向上、向下)PositionOfButtWeldFlatnessDirection(Upward,Downward)角焊缝位置向方向(向上、向下)PositionOfFilletWeldDirection(Upward,Downward)meameasur焊接速度(cm/min)8-12WeldingSpeed摆动焊或不摆动焊不摆动WeaveBeadWeldingOrNonweaveBeadWelding摆动参数/SinglePassWeldingOr/其他Others/7/SinglePassWeldingOr/其他Others/7855291870BendingTest试样TensionTestReportNo.PreheatingTsTWeaveBeadWeaveBeadParameter道焊道焊多道焊250250Multi-passWelding单单丝焊或多丝焊/Single/SingleWireWeldingOrMultiMultiWireWeldingCorrosionResistantCorrosionResistantOverlayWeldBrand..CSiMnP焊材牌号W焊材牌号WMSCr010500020.0.0.0.0.0.0.0.93/其他Others/NBT14-2011焊接工艺评定报告(PQR)//NBT14-2011焊接工艺评定报告(PQR)//号:TensionTestReportNo./拉伸试验TensionTestTensionTestReportNo./试验报告编号：试样编号SpecimenNo.试样宽度(mm)SpecimenWidth试样厚度(mm)SpecimenThickness横截面积(mm2)CrossSectionalArea断裂载荷(KN)FractureLoad抗拉强度(Mpa)TensileStrength断裂部位和特征FractureLocationAndBreakPerformance编号SpecimenNo.型SpecimenShape试样厚度 (mm)SpecimenThickness弯心直径 (mm)CenterOfBendD.弯心直径(°)AngleOfBend试验结果TestResultAcceptable///////试样编号SpecimenNoSpecimenDimension缺口类型NotchShape缺口位置NotchCocation冲击温度(℃)ImpactTemp冲击吸收功(J)备注Remarks试验报告编弯曲试验//////硬度检验试验报告编号：硬度检验试验报告编号：////Force///////////////根部:(焊透、未焊透)焊透根部:(焊透、未焊透)焊透焊缝:Weld:(Fusion、LackOfFusion)Weld、HeatAffectedZone:(Crack、FreeOfCrack)IfardnessIfardnessTestTensionTestReportNo.试样编号SpecimenNopecimenDimension母材硬度值HBBaseMetalHardnessValueWWeldHardnessValueHB热影响区硬度值HBHAZHardnessValueHBTestResultAcceptable无损检验：NDEExaminationRT/无损检验：NDEExaminationRT/UTMT/PT/结论：本评定按/规定焊接试件、检验试样、测定性能、确认试验记录正确ofweldingspecimen,performanceofspecimen,examinationandtestingrecord合格WelderWelder陈Welder’sWelder’sionion22PrepardeBy&PrepardeBy&DateviewedByviewedBy&DateAppdBy&AppdBy&Date05NB/T47014-2011