通领模具模流分析方案图ma-0159report

SIMULATIONREPORTMA201410-0159现代1410121Analyst:顾旺春Date:14.10.22ProductmodelintroductionAverageThickness：3.5

mmSize：129.48*245.47*34.84mmVolume：94.0182cm^3MaterialPC+ABS/CycoloyC6600:SABICInnovativePlasticsUS,LLC（替代料）ProcesssettingMelttemperature：260℃Moldtemperature：71℃Thickness

AnalysisIndicationMaterialDataThespecifiedmaterialisinMoldflowdatabase.Thepropertiesisshowninthepicturesbelow.InitialNozzle/GateLocationsandsizesBAABCDØ6~Ø10Ø10Ø9Ø3CG1DSimulationresultslistFilltime(contour)PressureatV/PswitchoverFlowFrontTempSystemPressureClampForceAirTrapsWeldLinesVolumetricshrinkageatejectionDeflectionConclusionsandsuggestionsFilltime图示为制品充填动态图，请双击图片以播放动画。Filltime图示为制品波前等高线图。图示红色为制品充填末端。Filltime=1.766sec。充填易发生短射Pressure

at

V/P

switchover图示为制品保压切换压力分布.制品在充填至98.02%时保压切换，切换压力为60.35Mpa.FlowFrontTemp图示为制品波前温度分布，制品大部分的波前温度均在材料允许范围内，易发生短射区域的波前温度相对较低，需注意加强排气。SystemPressure

Maxinjectionpressure=60.35Mpa。ClampForceMax.clampforceduringpacking=63.47tons。AirTraps图示显示制品积风位置，大多数积风出现在配合处，需用配合间隙排气。

Weldlines图示显示制品结合线位置。Volumetricshrinkageatejection图示显示制品顶出时的体积收缩，制品收缩较均匀、肉厚较厚处的收缩相对较大，需注意加强冷却。Deflection图示显示制品总变形趋势.变形值仅供参考。Deflection(X)图示显示制品X方向变形趋势。Deflection(Y)图示显示制品Y方向变形趋势。Deflection(Z)图示显示制品Z方向变形趋势。Conclusions&Suggestions

case

contentcaseFilltime1.766Spressure60.35MpaweldlineHavevolumetricshrinkageNon-uniformity以上分析结果仅供参考！综上所述：制品充填较平衡，易发生短射，易发生短射区域建议增加肉厚；制品大部分的波前温度均在材料允许范围内，易发生短射区域的波前温度相对较低，需注意加强排气；制品收缩较均匀、肉厚较厚处的收缩相对较大，需注意加强冷却；以上请确认。TheendThanks!以上分析结果均基于客户提供产品数据、模具信息及材料信息生成，若因提供的相关信息有误而生成的无效结果，YUDO将不承担任何责任。此份模流分析着重于确定热咀数量及位置，所以只采用普通工艺参数，没有经过优化，其分析结果仅供参考。分析报告中的