1、粉末冶金及金属陶瓷技术Powder Metallurgy and Metal Ceramics 粉末冶金模具 常用粉末冶金材料简介 粉末冶金制品结构工艺性 返回 粉末冶金是以金属粉末(或金属粉末与非金属粉末的混合物)为原料,通过成形、烧结或热成形制成金属制品或材料的一种冶金工艺技术。粉末冶金生产工艺与陶瓷制品的生产工艺类似,因此人们又常常称粉末冶金方法为“金属陶瓷法”。 粉末冶金材料或制品种类较多,主要有: 难熔金属及其合金(如钨、钨钼合金); 组元彼此不相溶、熔点十分悬殊的特殊性能材料(如钨铜合金型电触头材料); 难熔的化合物和金属组成的各种复合材料(如硬质合金、金属陶瓷)等。Powder
2、metallurgy is a metal powder (or a mixture of metal powder with non-metallic powder) as raw materials, molding, sintering or hot forming a metallurgical technology made metal products or materials. Similar to the powder metallurgy production process and production process of ceramics, so people ofte
3、n refer to the powder metallurgy method for metal ceramic method.More types of powder metallurgy materials or products are: refractory metals and their alloys (such as tungsten, tungsten - molybdenum alloy);-component immiscible with each other, between the melting point is very special properties o
4、f materials (such as tungsten - copper alloy electricalcontact material); refractory compounds and metal composition of the various composite materials (such as cemented carbide, cermet).粉末冶金的特点:1)某些特殊性能材料的唯一制造方法;2)可直接制出尺寸准确,表面光洁的零件,是少甚至无切削生产工艺;3)节约材料和加工工时,成本低。 4)制品强度较低;5)流动性较差,形状受限制;6)压制成形的压强较高,制品尺
5、寸较小;7)压模成本较高。The characteristics of the powder metallurgy:1) some special properties of materials, a unique manufacturing methods;2) can be prepared directly from the accurate size and smooth surface of the parts is less or even non-cutting production process;3) saving material and machining time an
6、d low cost.4) the lower strength products;5), poor mobility, shape restricted;6) compaction pressure is higher, smaller products;7) the high cost of die.粉末冶金基础 粉末冶金的主要工序有粉末制备、粉末预处理、成形、烧结及后处理等。粉末冶金材料或制品的工艺流程如图5-1所示。粉末性能和粉末制备粉末性能 固态物质按分散程度不同分成致密体、粉末体和胶体三类。 致密体或常说的固体:粒径在l 以上; 胶体微粒: 0.1 以下; 粉末体或简称粉末:介于二
7、者之间。Forming metal powders as an act of joining metal (forming metal contact between particles) in the cold state or with heating to low temperature may be studied taking account of the results obtained with cold welding of metals under pressure. As a basis for the hypothesis of metal joint formation
8、 without melting different mechanisms are assumed for contact formation. There are several hypotheses 6; recrystallization; diffusion; film; energy; dislocation; deformation; consideration of the occurrence of thermal-emf; connected with the level of electromagnetic emission; based on crystallograph
9、ic conformity between metals in contact. However, known and new experimental results cannot be described 金属粉末的性能对其成形和烧结过程以及制品的质量都有重大影响。金属粉末的性能可以用化学成分、物理性能和工艺性能来表征。 1. 粉末的化学成分 粉末的化学成分一般是指主要金属或组元的含量、杂质或夹杂物的含量以及气体的含量。 金属或合金粉末中的主要金属含量都不能低于98%99%。 粉末中的杂质主要指:1)与主要金属结合,形成固溶体或化合物的金属或非金属成分,如还原铁粉中的硅、锰、碳、硫、磷、氧
10、等;2)从原料和粉末生产过程中带进的机械夹杂,如二氧化硅、三氧化二铝、硅酸盐、难熔金属或碳化物等酸不溶物。Apart from obtaining perfect contact between particles at a certain stage of forming, an important role is also played by the mechanical component of strength in powder compaction 3. However, the effect of the mechanical component has hardly been
11、studied 12. In order to describe strength f.g for green compacts prepared by cold compaction of ductile metals the Barshin equation 2 is used: f.g = f.c.M. (1) Here f.c is the strength of compacted metal; is dimensionless contact cross section; M is the scale of f.g distortion taking account of para
12、meters described in 1 on which f.g depends and that is not in Eq. (1) = li Z = 2rel.g Z (2) 3)粉末表面吸附的氧、水汽和其他气体(N 2、CO2)。2.粉末的物理性能 粉末的物理性能:粉末颗粒大小和粒度组成、粉末颗粒形状与结构、显微硬度、粉末比表面、粉末真密度以及粉末颗粒的晶格状态。在技术条件中,通常只规定各级粉末颗粒的百分含量粒度组成或筛分组成 。1)颗粒形状:主要由粉末的生产方法决定,同时也与物质的分子或原子排列的结晶几何学因素有关;决定粉末工艺性能。2)粒度组成:指不同粒度的颗粒占全部粉末的百分含
13、量,又称粒度分布。3)粉末比表面:指每克粉末所具有的总表面积,通常用cm2/g或m2/g表示。 Physical properties of powder Physical properties of powder: powder particle size and particle size composition of the powder particle shape and structure, hardness, powder surface area, powder true density and powder particles of the lattice state. Te
14、chnical conditions, usually only requires that the percentage content of the powder particles at all levels - size composition or screening composition.1) particle shape: determined by the powder production methods, but also the substance molecules or atoms arranged in crystalline geometry factor; d
15、etermine the powder process performance.2) the size composition: refers to particles of different particle size accounts for the percentage content of all the powder, also known as the particle size distribution.3) powder surface area: Refers to the total surface area per gram of powder, usually cm2
16、 / g or m2 / g.3.粉末的工艺性能 粉末的工艺性能用粉末的松装密度、流动性、压缩性与成形性来表征。1)松装密度是指粉末试样自然地充填规定的容器时,单位体积内粉末的质量,单位为gcm3。2)流动性是50g粉末从标准的流速漏斗流出所需的时间,单位为s50g,其倒数是单位时间内流出粉末的重量,俗称为流速。3)压缩性代表粉末在压制过程中被压紧的能力,通常以在规定单位压力下粉末的压坯密度表示。4)成形性是指粉末压制后,压坯保持既定形状的能力,通常用粉末得以成形所需的最小单位压制力表示或用压坯强度来表示。 Powder technological properties of powder l
17、oose apparent density, fluidity, compressibility and formability to characterization.1) bulk density of the powder sample is naturally filling provisions of the container, the quality of the powder per unit volume, in units of g/cm3,2) mobility is the time required for 50g powder flow rate from the
18、standard funnel outflow unit s/50g its reciprocal outflow of the powder weight per unit time, commonly known as the flow rate.3) compression on behalf of the powder was pressed in the pressing process ability, usually in the green density of powder under the pressure of the provisions of the unit.4)
19、 forming means of powder compaction, the compacts ability to maintain a given shape, usually use the powder to be the smallest unit of forming the required pressing force expressed or green strength to represent. .粉末的制备 金属粉末的制取方法可分成两大类:机械法和物理化学法。 机械法是将原材料磨碎成粉而不改变原材料的化学成分的方法。如将金属切削成粉末颗粒;把金属研磨成粉末;液态金属
20、的制粒和雾化。 物理化学法是在制取粉末过程中,使原材料受到化学或物理的作用,而使其化学成分和集聚状态发生变化的工艺过程。还原金属氧化物、电解水溶液或熔盐、热离解羰基化合物、冷凝金属蒸汽、晶间腐蚀和电腐蚀法等。物理化学制粉法是以还原和离解等化学反应为基础的。 工业上普遍采用的有:氧化物还原法、电解法、热离解法、球磨法、涡旋研磨法、雾化法。 粉末的成形 成形方法 成形是粉末冶金工艺的重要步骤。成形的目的是制得具有一定形状、尺寸、密度和强度的压坯。粉末冶金常用的成形方法如下所示。模压成形是最基本方法。 松装烧结粉浆浇注模压成形热压成形等静压成形轧制成形离心成形挤压成形爆炸成形成形无压成形加压成形1.
21、粉末预处理 预处理包括:粉末退火,筛分,混合,制粒,加润滑剂等。 粉末的预先退火可使氧化物还原,降低碳和其他杂质的含量,提高粉末的纯度;同时,还能消除粉末的加工硬化、稳定粉末的晶体结构 。 筛分的目的在于把颗粒大小不同的原始粉末进行分级。 混合一般是指将两种或两种以上不同成分的粉末混合均匀的过程。混合可采用机械法和化学法。 制粒是将小颗粒的粉末制成大颗粒或团粒的工序,以此来改善粉末的流动性。 压制成形2.压制成形 压模压制是将置于压模内的松散粉末施加一定的压力后,成为具有一定尺寸、形状和一定密度、强度的压坯,如图5-2是压模示意图。 粉末的压缩过程一般采用压坯密度成形压力曲线来表示,如图5-3
22、所示。压坯密度变化分为三个阶段。滑动阶段:在压力作用下粉末颗粒发生相对位移,填充孔隙,压坯密度随压力增加而急剧增加;二是粉末体出现压缩阻力,即使再加压其孔隙度不能再减少,密度不随压力增高而明显变化;三是当压力超过粉末颗粒的临界压力时,粉末颗粒开始变形,从而使其密度又随压力增高而增加。 图5-2 模压示意图图5-3 压坯密度与压力 压坯密度分布不均匀:用石墨粉作隔层的单向压制实验,得到如图5-4所示的压坯形状,各层的厚度和形状均发生了变化,由图5-5可知在任何垂直面上,上层密度比下层密度大;在水平面上,接近上模冲的断面的密度分布是两边大,中间小;而远离上模冲的截面的密度分别是中间大,两边小。 因
23、为粉末体在压模内受力后向各个方向流动,于是引起垂直于压模壁的侧压力。侧压力引起摩擦力,会使压坯在高度方向存在明显的压力降。 a) 压制前 b) 压制后图5-4 用石墨粉作隔层的单向压坯 a)单向压制 b) 双向压制 图5-5 压坯密度沿高度分布图 为了改善压坯密度的不均匀性,一般采取以下措施: 1)减小摩擦力:模具内壁上涂抹润滑油或采用内壁更光洁的模具;2)采用双向压制以改善压坯密度分布的不均匀性,如图5-5所示;3)模具设计时尽量降低高径比。 粉末的压制一般在普通机械式压力机或液压机上进行。常用的压力机吨位一般为5005000kN。 如图5-6为双向压制衬套的4个工步示意图。 烧结 烧结是将
24、压坯按一定的规范加热到规定温度并保温一段时间,使压坯获得一定的物理及力学性能的工序。 烧结机理:粉末的表面能大,结构缺陷多,处于活性状态的原子也多,它们力图把本身的能量降低。将压坯加热到高温,为粉末原子所储存的能量释放创造了条件,由此引起粉末物质的迁移,使粉末体的接触面积增大,导致孔隙减少,密度增高,强度增加,形成了烧结。 固相烧结:烧结发生在低于其组成成分熔点的温度,如普通铁基粉末冶金轴承烧结。 液相烧结:烧结发生在两种组成成分熔点之间。如硬质合金与金属陶瓷制品的烧结。液相烧结时,在液相表面张力的作用下,颗粒相互靠紧,故烧结速度快、制品强度高。 烧结时的影响因素:烧结温度、烧结时间和大气环境
25、,粉末材料、颗粒尺寸及形状、表面特性以及压制压力等。 常用粉末冶金制品的烧结温度与烧结气氛见表5-1。烧结温度过高或时间过长,都会使压坯歪曲和变形,其晶粒亦大,产生所谓“过烧”的废品;如烧结温度过低或时间过短,则产品的结合强度等性能达不到要求,产生所谓“欠烧”的废品。 粉冶材料铁基制品铜基制品硬质合金不锈钢磁性材料(Fe-Ni-C0)钨、铝、钒烧结温度10502000700 9001350 1550125012001700 3300烧结气氛发生炉煤气,分解氨分解氨,发生炉煤气真空、氢氢氢、真空氢表5-1 常用粉末冶金制品的烧结温度与烧结气氛 后处理 后处理的方法按其目的不同,有以下几种:1)为
26、提高制件的物理及力学性能,方法有:复压、复烧、浸油、热锻与热复压、热处理及化学热处理。2)为改善制件表面的耐腐蚀性,方法有:水蒸气处理、磷化处理、电镀等。3)为提高制件的形状与尺寸精度,方法有:精整、机械加工等。4)熔渗处理,它是将低熔点金属或合金渗入到多孔烧结制作的孔隙中去,以增加烧结件的密度、强度、塑性或冲击韧度。 常用粉末冶金材料简介 粉末冶金常用来制作减摩材料、结构材料、摩擦材料、硬质合金、难熔金属材料、过滤材料、金属陶瓷、无偏析高速工具钢、磁性材料、耐热材料等。 硬质合金 硬质合金是粉末冶金工具材料的一种,主要用于制造高速切削硬而韧材料的刀具,制造某些冷作模具、量具及不受冲击、振动的
27、高耐磨零件。1.硬质合金的性能特点 1)具有很高的常温硬度(6981HRC),高的热硬性(可达9001000),优良的耐磨性。2)具有高的抗压强度(可达6000 MPa),但抗弯强度较低;3)良好的耐蚀性(抗大气、酸、碱等)和抗氧化性;4)线膨胀系数小。 2.切削加工用硬质合金分类、分组代号 切削加工用硬质合金按其切屑排出形式和加工对象的范围可分为三个主要类别,分别以字母P、M、K表示。 P适用于加工长切屑的黑色金属,以蓝色作标志; M适于加工长切屑或短切屑的黑色金属和有色全属,以黄色作标志; K适于加工短切屑的黑色金属、有色金属及非金属材料,以红色作标志。切削加工用硬质合金用途分组代号与硬质
28、合金牌号对照见表5-2,表5-3。 3.硬质合金的应用 1)用作刀具材料。硬质合金作刀具材料的用量最大,如车刀、铣刀、刨刀、钻头等;2)用作模具材料。用硬质合金作模具主要是指冷作模,如冷拉模、冷冲模、冷挤模和冷镦模等;3)用作量具及耐磨零件。如千分尺、块规、塞规等。 含油轴承材料 含油轴承材料是一种具有多孔性的粉末冶金材料,常用以制造轴承零件。这种材料压制成轴承后,放在润滑油中浸润,由于粉末冶金材料的多孔性,在毛细现象作用下,可吸附大量润滑油(一般含油率为12%30),故称为含油轴承。 常用的含油轴承有铁基和铜基含油轴承两类。1)铁基含油轴承是铁-石墨(0.5%)粉末冶金材料或铁-硫(0.5%
29、1)-石墨(1%2)粉末冶金材料;铁-石墨粉末冶金材料的组织为珠光体(大于40%)十铁索体十渗碳体(小于5%)十石墨+孔隙,硬度30110HBS。铁-硫-石墨粉末冶金材料的组织除了与铁-石墨粉末冶金材料相同的组织以外还有硫化物,可进一步改善摩擦条件,硬度为3570 HBS。2)铜基含油轴承常用的是青铜粉末与石墨粉末制成的冶金材料,它具有较好的热导性、耐蚀性抗咬合性,但承压能力较铁基含油轴承小。 含油轴承材料一般用于制作中速、轻载荷的轴承,尤其适宜制作不能经常加油的轴承,如纺织机械、电影机械、食品机械、家用电器(如电风扇、电唱机)等的轴承,在汽车、拖拉机机床电机中也得到广泛应用。 粉末冶金制品及金属陶瓷结构工艺性 考虑粉末冶金零件结构工艺性时,总的原则是零件应尽量平整简单,即不带倒角、尖角、凸起、凹槽以及难于直接压制或脱模出的内、外螺纹、倒锥度、与压制方向垂直的孔、槽等。一般需要从压制困难性、脱模困难性、粉末均匀填充困难性和压模强度、寿命等诸方面考虑。 考虑压制困难性及简化模具 零件的内、外螺纹、倒锥度、与压制方向垂直的孔、槽等均不能直接压制出 。图5-10a中与压制方向垂直的退刀槽需改为图5-10b的结构;图5-11a所示零件,应在模具上做出垫块
温馨提示
- 1. 本站所有资源如无特殊说明,都需要本地电脑安装OFFICE2007和PDF阅读器。图纸软件为CAD,CAXA,PROE,UG,SolidWorks等.压缩文件请下载最新的WinRAR软件解压。
- 2. 本站的文档不包含任何第三方提供的附件图纸等,如果需要附件,请联系上传者。文件的所有权益归上传用户所有。
- 3. 本站RAR压缩包中若带图纸,网页内容里面会有图纸预览,若没有图纸预览就没有图纸。
- 4. 未经权益所有人同意不得将文件中的内容挪作商业或盈利用途。
- 5. 人人文库网仅提供信息存储空间,仅对用户上传内容的表现方式做保护处理,对用户上传分享的文档内容本身不做任何修改或编辑,并不能对任何下载内容负责。
- 6. 下载文件中如有侵权或不适当内容,请与我们联系,我们立即纠正。
- 7. 本站不保证下载资源的准确性、安全性和完整性, 同时也不承担用户因使用这些下载资源对自己和他人造成任何形式的伤害或损失。
最新文档
- 幕墙工程售后服务承诺书(35篇)
- 《榜样的力量》观后感(5篇)
- DB12-T 1072-2021 呼吸道传染病集中隔离医学观察点消毒技术指南
- 茶文化与茶艺鉴赏 教案 项目四 知茶性-茶叶基础知识
- 2024年碳金融项目资金申请报告代可行性研究报告
- 华中科技大学建规学院设计素描教案
- 供应链运营 教案项目一 供应链及供应链管理
- 新建民用装配式建筑防护设计与施工技术规范征求意见稿
- 中小学生防火安全主题班会教案
- 上海市县(2024年-2025年小学五年级语文)统编版竞赛题(下学期)试卷及答案
- T-ESD 3008-2021 热固性防静电粉末涂料通用规范
- 2023年四川农信校园招聘笔试题库及答案解析
- 液压传动课程设计-专用铣床液压系统
- 浮点数运算方法
- YS/T 591-2006变形铝及铝合金热处理
- 第9讲:为新中国而奋斗
- GB/T 31883-2015道路车辆牵引连接件、牵引杆孔、牵引座牵引销、连接钩及环形孔机械连接件使用磨损极限
- GB/T 23679-2009集装箱机械箱封
- GB/T 23505-2017石油天然气工业钻机和修井机
- 公务员职业道德与行为规范课件
- 初中英语-名词-单复数-练习题-含答案
评论
0/150
提交评论