各种橡胶的基础配方

1、附表1各种橡胶的根底配方附表1-1天然橡胶NR根底配方一原材料名称ASTMASTMASTM原材料名称纯胶配合炭黑配合无硫配合NR100.00100100NR( RSS3)100100100氧化锌5.0066氧化锌355硬脂酸2.000.50.5硬脂酸233硫黄2.503.53.5硫黄2.52.5防老剂PBN1.00促进剂DM0.70.7促进剂DM1.00M0.5TBBS0.7促进剂TT3防老剂D111HAF5050芳炷油33硫化条件140 C X10min,20min , 40min,80min硫化条件138 C >60min138 C >60min138 C >60min附

2、表1-2 天然橡胶NR根底配方二原材料名称根本配方根本配方试验配方试验配方试验配方纯胶配合纯胶配合纯胶配合纯胶配合炭黑配合NR (SCR)100100100100100氧化锌55665硬脂酸0.51.50.50.52硫黄32.53.53.52.25促进剂M0.70.5促进剂CBS0.5促进剂TBBS0.70.7HAF (N378)35合计109.2109.5110.5110.7144.95硫化条件143 C >25min143 C X25min附表1-3异戊橡胶IR根底配方原材料名称ASTM高耐磨炭黑HAF 配方原材料名称国内IR100IR100氧化锌5氧化锌5硫黄2.25硬脂酸3硬脂酸

3、2硫黄2促进剂NS0.7促进剂CZ0.7HAF35防老剂D1HAF50芳炷油3硫化条件135 C >20min , 30min , 40min , 60min硫化条件140 C >60min附表1-4 丁苯橡胶SBR根底配方ASTM 一原材料名称非充油SBR配方充油SBR配方充油量25phr充油量37.5phr充油量50phr充油量62.5phr充油量75phr非充油SBR100充油SBR125137.5137.5150162.5175氧化锌33.754.1234.54.885.25硬脂酸11.251.3811.51.631.75硫黄1.752.192.421.752.632.85

4、3.06炉法炭黑5062.568.7568.757581.2587.5促进剂NS11.251.381.381.51.631.75硫化条件145 C >25min , 35min, 50min145 C X25min, 35min, 50min145 C X25min , 35min, 50min145 C X25min , 35min , 50min145 C X25min , 35min, 50min145 C X25min,35min, 50min N-叔丁基-2-苯并嚷晚次磺酰胺. phr指每百质量份橡胶的质量份数.附表1-5 丁苯橡胶(SBR)根底配方(二)原材料名称标准 SBR

5、 (1500)充油 SBR (1712)溶聚 SBR-18 (1000)溶聚 SBR-25 ( 1204)SBR100137.5100100氧化锌3333硬脂酸2222硫黄221.81.8促进剂CZ1111HAF50505050操作油455硫化条件145 C >60min140 C >60min140 C >60min140 C X60min附表1-6 氯丁橡胶(CR)根底配方原材料名 称ASTM 纯胶配方ASTM 半补强炉黑(SRF)配方原材料名 称W型纯胶 配合W型填料 配合G型纯胶 配合G型填料 配合国标硫调 型国标混合型CR ( W型)100100CR10010010

6、0100100100氧化镁44氧化锌555555硬脂酸0.51硬脂酸0.50.50.50.50.50.5SRF29氧化镁444444氧化锌55促进剂NA-220.50.5促进剂NA-220.350.5防老剂PA1111防老剂D22SRF3030硫化条件150 °C X15 ,30 , 60min硫化条件153 °C >30min153 °C X30min153 C >30min153 C >30min附表1-7 丁基橡胶(IIR)根底配方原材料名称ASTM 纯胶配方ASTM 槽黑配方ASTM 炉黑配方ASTM 卤化丁基原材料名称纯胶配合炭黑配合醍

7、肪配合树脂配合IIR100100100100IIR100100100100氧化锌5535氧化锌5555硫黄221.75硬脂酸2231硬脂酸一311硫黄21.52促进剂DM0.5对醍二肪2促进剂TMTD111酚醛树脂12槽法炭黑50促进剂TT1.51.5HAF5040促进剂M0.50.5聚对二亚硝基苯0.2CR0.3三氧化二 铁10GPF60FEF6060石蜡油2020硫化条件150 °C X20min , 40min , 80min150 C X25min ,50min ,100 min硫化条件153 C X10min153 C X10min145 C *0 min160 C >

8、;90min生产中可使用硬脂酸锌,因此纯胶中可不使用硬脂酸.附表1-8 丁睛橡胶(NBR)根底配方原材料名称ASTM瓦斯炭黑配方HAF炭黑配方原材料名称170427073604NBR100100NBR100100100100氧化锌53氧化锌5555硬脂酸11硬脂酸11.51.51.5硫黄1.51.5硫黄1.2521.51.5促进剂DM1NS 0.7促进剂TS0.3M 1.5M 0.8M 0.8瓦斯炭黑40HAF 40SRF40瓦斯炭黑504545合计146.2160153.8153.8硫化条件150 C X10min , 20min , 40 min, 80 min硫化条件153 C >

9、60min附表1-9 顺丁橡胶(BR)根底配方原材料名称ASTM干生胶充油胶原材料名称BR1220BR100100+yBR100氧化锌33氧化锌3硬脂酸22硬脂酸2硫黄1.51.5硫黄1.8促进剂NS0.90.009 X (100+y)促进剂CZ1HAF600.6 X( 100+y)HAF50ASTM 型 103 油15防老剂D1182.4操作油5硫化条件145 C>25min , 35min, 50min硫化条件145 C X60min附表1-10 三元乙丙橡胶EPDM 根底配方原材料名称ASTM原材料名称EPMEPDMEPDM100100EPR100100氧化锌55氧化锌55硬脂酸1

10、1硬脂酸1促进剂M0.50.5硬脂酸钙1促进剂TMTD1.51硫黄0.31.5硫黄1.51.5DCP2.6HAF5080促进剂TT1.5环烷油1550促进剂M0.5HAF50合计230硫化条件见注硫化条件160 C >30min160 C >30min注：硫化条件在第三单体为 DCDP时为160 C X30min , 40 min ;第三单体为 ENB时为160 C X10 min, 20min.附表1-11氯磺化聚乙烯CSM根底配方原材科名称ASTM黑色配方ASTM白色配方CSM40CSM20CSM100100100100SRF405050一氧化铅252020活性氧化镁4促进剂D

11、M0.50.50.5促进剂DPTT2222二氧化钛3.5碳酸钙50季戊四醇3防老剂NBC33碳酸镁2020操作油1010硫化条件153 C>30min , 40min , 50min153 C>30min, 40min, 50min153 C >30min153 C W0min附表1-12 氯化丁塞橡胶CIIR根底配方原材料名称ASTMCIIR100硬脂酸1促进剂DM2氧化镁2HAF50促进剂TMTD1氧化锌3硫化条件153 °CX30min, 40min , 50min.附表1-13 聚硫橡胶(PSR)根底配方原材料名称ST配方ASTMFA配方ASTM原材料名称金

12、属氧化物硫化醍肪硫化PSR100100TFA100SRF6060TST100硬脂酸10.5氧化锌100.5过氧化锌6硬脂酸0.53氧化锌10对醍二肪1.5促进剂DM0.3促进剂D0.1促进剂DPG0.1促进剂DM0.3SRF4060硫化条件150 C X30 , 40 , 50min150 C X30 , 40 , 50min硫化条件148 c >40min141 C >30min 该胶主要单体为二氯乙基缩甲醛,系美国固态聚硫橡胶牌号,不塑化也能包辗. 该胶主要单体为二氯乙烷、二氯乙基缩甲醛,系美国固态聚硫橡胶牌号,必须通过添加促进剂,在 混炼前用开炼机薄通,进行化学塑解剂而塑炼.

13、附表1-14 丙烯酸酯橡胶(ACM )根底配方原材料名称ASTM原材料名称TCY硫化S/SOAP硫化ICA硫化ACM100ACM100100100快压出炭黑(FEF)60三硫化割脉酸0.5硬脂酸钾0.75促进剂BZ1.5防老剂RD1促进剂二乙基硫服0.3硬脂酸钠1.75硫黄0.3硫黄0.25硬脂酸钠0.3硬脂酸钾0.5异割脉酸0.5十八基三甲基漠 化铉1.8二苯硫脉1.3硬脂酸111FEF606065脂肪酸酯1防老剂222防焦剂PVI (CTP)0.2硫化条件一 段硫化166CX10min；二 段硫化180 C X8h170 C X20min170 C X20min170 C >20mi

14、n附表1-15混炼型聚氨酯橡胶(PUR)根底配方原材料名称ASTM原材料名称硫黄硫化DCP硫化AUPUR100PUR100100100古马隆15硫黄1.5促进剂M1DCP1.53.5促进剂DM4活性剂0.35SA 0.2促进剂Caytur40.35促进剂DM3硫黄0.75促进剂M1HAF30易混槽黑3030SRF 30硬脂酸镉0.5硫化条件153CX0min,60min硫化条件153 C X60min153 C >60min151 C >40min 选择AdipreneCM (美国Dupont公司产品牌号) 促进齐ij DM与氧化锌的复合物.表附表1-16氯醇橡胶(CO)根底配方原

15、材料名称ASTM瑞翁CO国外ECO原材料名 称硫脉硫化(CO )CHR胺硫化(ECO )CHC国产CO国产ECOGCO氯醍橡胶100100100氯醍橡胶100100100100硬脂酸铅2TETA2FEF3030NA-221.51.51.5铅丹1.555促进剂DM2防老剂NBC22硬脂酸锡1.5促进剂NA-221.21.5硬脂酸锌11硬脂酸锡2铅丹5555六亚甲基氨基甲酸二胺0.75防老剂NBC1222二丁基二硫代氨基甲酸锌1FEF4040HAF50HAF50增塑剂TP701硫化条件160 C >30m in, 40min, 50min155 C *0m155 C X30 min165 C

16、 X6mi n硫化条件155 C X30m in155 C X30m in附表1-17 氟橡胶(FKM )根底配方原材料名称ASTM原材料名称过氧化物硫化(23 型)胺硫化(26型)酚硫化(246型)FKM (Viton 型)100氟橡胶100100100中粒热裂炭黑(MT)20BP3氧化镁15二碱式亚磷酸铅10硫化剂Diak3#3.0氧化锌10N,N'-二亚肉桂基 -1,6-己二胺(3号 硫化剂)3氧化镁15双酚AF0.8节基三苯基氯化 磷2氢氧化钙5硫化条件一段硫化150 C X30min二段硫化250 C X24h一段硫化143 C X30min二段硫化150 °C X16h一段硫化150 C >30min二段硫化200 C X16h一段硫化160 C >