钢材抗拉强度与硬度的对照表

1、根据德国标准DIN50150,以下是常用范围的钢材抗拉强度与维氏硬度、布氏硬度、洛氏硬度的对 照表。抗拉强度Rm N/mm2维氏硬度HV布氏硬度HB洛氏硬度HRC2508076.0-2708580.7-2859085.2-3059590.2-32010095.0-33510599.8-350110105-370115109-380120114-400125119-415130124-430135128-450140133-465145138-480150143-490155147-510160152-530165156-545170162-560175166-575180171-5951851

2、76-610190181-625195185-640200190-660205195-675210199-690215204-705220209-720225214-740230219-755235223-77024022820.378524523321.380025023822.282025524223.183526024724.085026525224.886527025725.688027526126.490028026627.191528527127.893029027628.595029528029.296530028529.899531029531.0103032030432.21

3、06033031433.3109534032334.4112535033335.5111536034236.6119037035237.7122038036138.8125539037139.8129040038040.8132041039041.8135042039942.7138543040943.6142044041844.5145545042845.3148546043746.1152047044746.91555480(456)47.71595490(466)48.41630500(475)49.11665510(485)49.81700520(494)50.51740530(504

4、)51.11775540(513)51.71810550(523)52.31845560(532)53.01880570(542)53.61920580(551)54.11955590(561)54.71995600(570)55.22030610(580)55.72070620(589)56.32105630(599)56.82145640(608)57.32180650(618)57.866058.367058.868059.269059.770060.172061.074061.876062.578063.380064.082064.784065.386065.988066.490067

5、.092067.594068.0HB有两种一种是HBS （钢球）另一种是HBW （硬质合金球）用一定直径的钢球或硬质合金球，以规定的试验力（ F）压入式样表面，经规定保持时间后卸除试验力，测 量试样表面的压痕直径（L）。布氏硬度值是以试验力除以压痕球形表面积所得的商。以HBS（钢球）表示，单位为 N/mm2（MPa）其计算公式为：式中：F-压入金属试样表面的试验力，N;D-试验用钢千直径,mmd-压痕平均直径，mm测定布氏硬度较准确可靠，但一般HBS只适用于450N/mm2（MPa以下的金属材料，对于较硬的钢或较薄的板材不适用。在钢管标准中，布氏硬度用途最广，往往以压痕直径d来表示该材料的硬度，既直观，又方便。 布氏硬度试验还可用于有色金属和软钢，采用小直径球压头可以测量小尺寸和较薄材料。布氏硬度计多用于原材料和半成品的检测，由于压痕较大，一般不用于成品检测。举例：120HBs10/1000/30 :表示用直径10mml球在1000Kgf （9.807KN）试验力作用下，保持30s （秒）测得的布氏硬度值为 120N/ mm2 （MP