聚丙烯腈纤维生产工艺路线简述

聚丙烯腈纤维生产工艺路线简述目录CONTENTS01腈纶生产工艺路线02NaSCN一步法（湿法纺）DMF干法（二步法）0305主要溶剂04工艺路线比较腈纶生产工艺路线1腈纶生产工艺路线(ProcessFlow)聚合(polymerization)纺丝(spinning)一步法(onestep)

二步法(twostep)湿纺(wetspinning)

干纺熔纺湿纺干喷湿法纺NaSCNDMFZnCl2DMSOHNO3

溶剂(solvent)DMADMFDMAECHNO3NaSCNDMF

(dryspinning)(meltspinning)

(wetspinning)

(dry-wetspinning)均相溶液聚合(homogeneoussolutionpolymerization)非均相聚合

(heterogeneoussolutionpolymerization）NaSCN一步法(湿法纺）2第一单体(firstmonomer)第二单体(secondmonomer)第三单体(thirdmonomer)溶剂（NaSCN溶液）(solvent)引发剂（AIBN）(initiatingagent)浅色剂（TUD）(lightcolouragent)匀温计量(metering)混合(blending)聚合(polymerization)脱单(demonomer)聚合工序(polymerization)后加工工序(after-treatment;reprocessing)牵伸(stretching)水洗上油(washingandoiling)

干燥

(drying)卷曲(crimping)切断(cutting)打包(packing)纺丝(spinning)纺丝工序(spinning)混批(blending)脱泡(deaeration)过滤(filtration)原液制备(preparationofspinningsolution)DMF干法（二步法）3第一单体(firstmonomer)第二单体(secondmonomer)第三单体(thirdmonomer)酸性水溶液（SO2）（acidicsolution）活性剂(activeagent)引发剂(initiatingagent)聚合工序(polymerization)混合计量

(metering)聚合

(polymerization)聚合物水洗过滤

(washingandfilteration)聚合物干燥(drying)聚合物贮存(storing)牵伸(stretching)水洗上油

(washingandoiling)干燥

(dryingandsetting)卷曲(crimping)切断(cutting)打包(packing)后加工工序（after-treatment;reprocessing)纺丝工序(spinning)聚合物溶解(dissoving)过滤脱泡(filtrationanddeaeration)原液制备(preparationofspinningsolution)工艺路线比较4聚丙烯腈纤维生产工艺路线比较：一步法与二步法：一步法是指PAN的合成采用溶液聚合，聚合物不经分离，直接配成纺丝原液去纺丝；二步法又称为水相沉淀聚合路线。PAN的合成采用水相沉淀聚合，聚合物经分离后重新溶解，即聚合物的制备及原液配制两步完成；腈纶的成形借助于蒸发除去挤出细流中的溶剂，称为干法纺丝；借助于挤出细流中的溶剂与凝固浴中溶剂的双向扩散，称为湿法纺丝。干法纺丝与湿法纺丝：主要溶剂5二甲基甲酰胺（DMF）是一种透明液体，能和水及大部分有机溶剂互溶。它是化学反应的常用溶剂。纯二甲基甲酰胺是没有气味的，但工业级或变质的二甲基甲酰胺则有鱼腥味，因其含有二甲基胺的不纯物。DMFDMA化学名称：N,N-二甲基乙酰胺二甲基乙酰胺是一种强极性非质子化溶剂，能溶解多种化合物，与水、醚、酮、酯等完全互溶，具有热稳定性高、不易水解、腐蚀性低、毒性小等特点，对多种树脂，尤其是聚氨酯树脂、聚酰亚胺树脂具有良好的溶解能力，可用作耐热合成纤维、塑料薄膜、涂料、医药、丙烯腈纺丝的溶剂。二甲基乙酰胺作为一种低毒、高沸点、高极性的非质子溶剂和化工中间体，在合成材料、医药、农药、化纤、石油加工及有机颜料等领域有着广泛的应用。DMSO二甲基亚砜（Dimethylsulfoxide或DMSO），无色液体，重要的极性非质子溶剂。它可与许多有机溶剂及水互溶。二甲基亚砜具有极易渗透皮肤的特殊性质，造成使用人员感觉类似牡蛎般的味道。EC碳酸乙烯酯是透明无色液体(>35℃