世界针灸学大会报告：方便揿针原始效应物质研究

针刺原始效应物质的研究

StudyonAcupunctureOriginalMaterial

世界针灸学会联合会成立20周年庆典暨世界针灸学术大会讲演稿张大同杨肖娥1王樟连2郑振洨王海明李廷强1冯英1沈瑾王芸2（杭州市第三医院，杭州310002；1浙江大学，杭州310027；2浙江中医药大学，杭州310053）(ZHANGdatong,YANGXiaoe1,WANGZhanglian2,ZHENGZhenxiao,WANGHaiming,LITingqiang1,FENGYing1,SHENJin,WangYun2（ThirdHospitalofHangzhou,310002；1ZhejiangUniversity,310027；2ZhejiangChineseMedicalUniversity310053,Hangzhou,ZhejiangProvince，PR.China）

目的

将下述4项实验所取得的证据及电化学、微观腐蚀原电池效应科学规律，共同组成一个完整的证据锁链，证明针行方便揿针针刺原始效应物质、针刺电化学效应机制。ObjectiveWewillpracticethefollowingFourexperimentsmadebytheevidence,electrochemicalandcorrosionoriginalmicro-batteryeffectscientificlaws,thecommoncompositionofacompletechainofevidence，andwillprovethattheeffectofacupuncturerawmaterials,electrochemicaleffectsofacupuncturemechanism.实验1针行方便揿针针刺电化学电流研究

实验1-1人体针刺电化学电流研究Experiment1-1Electrochemicalcurrentstudybyacupuncture方法将针行方便揿针分别垂直刺入实验对象的肩髃、肩髎穴位中，用数字显示电流仪测量记录产生的电流变化MethodsAcupunctureneedleswerestungverticallytoalienateexperimentsofthepointsofJianyu,Jianliao,withfigurescurrentmeasurementrecordsshowedthechangesofthecurrent.结果

针行方便揿针刺入人体穴位，所测的9名对象电流变化在-44~67μA区间，电流差值为27~73μA。ResultStainlesssteelacupuncturewereneedledintothehumanbody,measuringthechangesonthecurrenttargetis-44~67uAinterval,thecurrentmarginwas27~73µAonthecaveof9cases.表1-1、针刺肩髃、肩髎穴的电流测定记录表（男=m、女=w）

Table1、StatisticsofelectriccurrentmeasuredinthepointofJianYu、Jianliaoinserted（Man=m、Woman=w）N性别年龄（岁）电流变化（μA）电流差值（μA）峰值出现（次）Sexage（years）electriccurrentelectriccurrentdifferencepeakvalue1w69-20～133342m52-9～435253w65-44～186254m78-37～165365w75-4～232746w77-6～677347m72-24～487258w54-12～395159m23-25～47726实验1-2动物针刺电化学电流研究方法将12只ICR实验小鼠按其存活及处死（强力颈椎脱位法）后的整个时间过程分为：A组（健康活体），B组（死亡1h），及C组（死亡28h）；先将针行方便揿针分别刺入每只经麻醉的ICR实验小鼠左侧的曲池与后三里穴，用数字显示电流仪测量观察2min并记录产生的电流变化，后将该小鼠处死；待该小鼠处死1h、28h后再分别对其右侧的曲池与后三里穴，并用数字显示电流仪测量观察2min并记录产生的电流变化；记录的数据再制表分析。结果

针刺实验小鼠A组的所发电流在83~1μA区间，并一直呈现由高向低的电流变化，电流发生率为100％，电流的平均差值为35.92μA；B组所发电流在41~-1μA区间，并一直呈现由高向低的电流变化，电流发生率为100％，电流平均差值为21.58μA；C组所发电流在148~1μA区间，一直呈现由高向低的电流变化，电流发生率为100％，电流平均差值为68.92μA。

表1-2、12只小鼠活时及死后针刺曲池、足三里穴所发电流发生率分析表（μA）No 体重gA组A组差值B组B组差值 C组 C组差值1 19.428~62224~0 24 120~37 832 18.521~41723~3 20 102~43 593 19.136~2349~-1 10 123~67 564 21.236~92734~2 32 43~8 355 18.315~21316~7 09 59~13 466 20.083~28138~3 35 96~18 787 18.358~85041~6 35 38~12 268 19.734~43031~1 30 148~40 1089 17.961~85312~2 10 112~1 11110 20.059~15824~2 22 89~3 8611 17.323~32011~0 11 104~28 7612 18.528~22626~5 21 93~30 63合计228.283~143141~-1259 148~1 827均数19.02 35.92 21.58 68.92发生率 100％ 100％ 100％ 分析证明该实验所测电流为针刺电化学效应的依据如下：AnalysisThecurrentexperimentprovidesfortheevidenceontheeffectsofacupunctureelectrochemical.A、由于无皮肤的组织电阻为300~800Ω·㎝，因此实验1-1所测到的-44~67μA瞬间电流变化区间的电流差值为27~73μA。而其瞬间电压变化区间（根据欧姆定律）应为：8.1V~58.4V，明显远远大于50~100mV的细胞动作电位；因此该瞬间电流不是我们已知的生物内在电流。

而实验1-2所测的83~1μA、41~-1μA、148~1μA瞬间电流变化区间的平均电流差值为35.92μA、21.58μA、21.58μA，并一直呈现由高向低的电流变化，电流发生率为100％，应与上述实验1-1的结果相同。A、Theorganizationskinresistancewas300to800Ω•cmonwithoutskin,sothemarginoftransientcurrentchangeswas27~73µAontheinterval-44~67μA.Whiletheinstantaneousvoltage(accordingtoOhm'slaw)was8.1V~58.4V,obviouslyfargreaterthanthe50~100mVofactionpotentials；Assuch,thecurrentwasnotbiologicalinternalcurrentsasweknow。B、此外，笔者曾在2002年的离体动植物（猪肉、草莓）电化学测定实验中也明显证实了（结果与此次活体实验一样）其间也能产生uA级的电流。B、Inaddition，theresultalsowasprovedbyinvitroelectrochemicalplantsandanimalsoftheexperimentin2002(withthesamevivoexperiments)whichcouldalsohaveaClassAμAElectricity.C、针行方便揿针电化学科学规律。

C、Theexistingelectrochemicaluniversallawsofscience.实验1

结论

针刺穴位组织（能改变电位差）具有电化学原电池效应。Experiment1

ConclusionAcupuncturepoints(tochangethepotentialdifference)havetheoriginalbatteryelectrochemicaleffect.实验2

方便揿针针体的腐蚀研究Experiment2Clinicalstudiesofacupunctureneedlescorrosion（Thecontrolgroupdidnotjoinbecauseoforiginallimitedtothelength,itwasaddedasfollows）方法将3600枚针行方便揿针随机分成实验组（3000枚）和对照组（600枚），在一年中，实验组的3000枚针行方便揿针在临床反复灭菌使用，对照组600枚针行方便揿针也随实验组一起反复灭菌但不使用，其间由目测挑选出具有可见腐蚀斑的揿针（数据采用x2检验处理，P＜0.05有统计学意义），再选典型腐蚀的揿针用电子显微镜放大拍摄分析。Methods3,600acupunctureneedlesweredividedintotheexperimentalgroup(3000)andthecontrolgroup(600)randomly.3000acupunctureneedleswereusedrepeatedlybysterilization,and600acupunctureneedlesweresterilizedagainandagainastheexperimentalgroupbutwithoutusing，too.Meantime,selectedcorrosionspotwiththeacupunctureneedlebythevisualvisible(dataprocessingusingx2test,P<0.05wassignificantly),there-electionoftypicalcorrosionacupunctureneedlestobeamplifiedwithelectronicmicroscope.结果目测出实验组腐蚀针259枚（电子显微镜：腐蚀针行针灸针表面呈现部分较严重腐蚀缺损区域），而对照组目测腐蚀针为0枚；实验组与对照组比较，P＜0.05差异有显著意义。请见具体资料。Result259

needleswerecorrodedintheexperimentalgroup(electronmicroscope:acupunctureneedlesurfacecorrosionshowedsomeofthemoreseriouscorrosiondefectregions),while0needlewascorrodedinthecontrolgroupbyeyeballing;Theresultofexperimentalgroupcomparedwiththecontrolgroup,P<0.05significantdifference.Seespecificinformation.表2、实验组针行方便揿针针体目测腐蚀率发生分析表

Table2、Theexperimentalgroupstainlesssteelacupunctureneedlesvisualanalysisofcorrosionrateintable时间（月）腐蚀针数未腐蚀针数分析总针数腐蚀百分率％Time（Amonth）CorrosionpincountsNocorrosionpincountsThetotalnumberofneedleCorrosionpercentage％1～303000300004～619298130000.637～951293029811.7110～12189274129306.45Total259274130008.63表3、实验组与对照组目测针行方便揿针腐蚀率的比较

Table3、Theexperimentalgroupandcontrolgroupvisualstainlesssteelacupunctureneedlecorrosionratecomparison腐蚀针数未腐蚀针数分析总针数腐蚀百分率％CorrosionpincountsNocorrosionpincountsThetotalnumberofneedleCorrosionpercentage％实验组259（8.63）2741（91.37）30008.63(Theexperimentalgroup)对照组0（0）600（100）6000(Thecontrolgroup)Total259334136007.19x2=55.81562406P＜0.05腐蚀揿针的电子显微镜照片所示腐蚀现象见图1、2、3CorrosionacupunctureneedleshownintheelectronmicroscopephotographsofcorrosionphenomenonSeefigure1,2,3图1放大50倍的腐蚀针行方便揿针局部

Figure1Large50timesthelocalcorrosionacupunctureneedles图2放大100倍的腐蚀针行方便揿针局部

Figure2Large100timesthelocalcorrosionacupunctureneedles图3放大1000倍的腐蚀针行方便揿针局部

Figure3Large1000timesthelocalcorrosionacupunctureneedles

实验2

结论

针行方便揿针针刺穴位组织会使针体腐蚀，该腐蚀现象符合电化学腐蚀原理。Experiment2ConclusionThepointofacupunctureneedleswillcorrodetheacupunctureneedles,corrosionphenomenonisconsistentwiththeprincipleofelectrochemicalcorrosion.实验3

针行方便揿针针刺穴位组织铬、镍、铁元素含量变化的研究Experiment3ThestudyonthechangeofelementofacupuncturePointswithchromium,nickel,iron.方法将15只实验兔按A（揿针10枚刺入左环跳穴区电针仪通电留针5h）、B（揿针10枚刺入右臂臑穴区留针5h）实验组及C（右环跳穴区）、D（右臂臑穴区）对照组，进行实验，5h后对60个（每点15个）样本用(ICP-MS)电感耦合等离子体质谱仪（对与方便揿针主体相关联的铬、镍、铁元素的含量）进行分析，数据采用t检验处理，P＜0.05有统计学意义。Methods15rabbitsweredividedintotheexperimentalgroupsandcontrolgroups，theexperimentalgroupswereA(10acupunctureneedlespiercingleftCentralPointdistrictjump-electro-acupunctureneedletelegramtostay5h)，andB(10acupunctureneedlespiercingrightarmHDLPointsdistricttostay5h).ThecontrolgroupswereC(rightringjumpPoint),andD(rightarmHDLPointdistrict.60samples(15perpoint)wereanalyzedbyelectricityflucoupledplasmamassspectrometer(withstainlesssteelacupunctureneedleslinkedtothemainchromium,nickel,ironcontent),dataprocessingusingt-test,P<0.05withstatisticalsignificance.结果实验组铬、镍、铁元素含量大幅升高，与对照组比较，P＜0.001其差异具显著意义。见表4、表5。ResultTheexperimentalgroupchromium,nickel,ironcontentsignificantlyincreased,comparedwiththecontrolgroup,P<0.001withitssignificantdifference.SeeTable4andTable5.表4两组臂臑穴区铬、镍、铁元素含量的比较

（±S，ng/g，各组n=15）

Table4、CompareofnumberofCr、Ni、FeinthepointofJianYubetweentwogroups铬Cr镍Ni铁Fe实验组（留针）270.01682±71.63116.16087±43.8727060.804±11332.91

(stayneedle)对照组Control54.007090±12.762.7388872±1.9495523.4536±2380.729Comparedwiththecontrolgroup（与对照组比较）:P＜0.001表5两组环跳穴区铬、镍、铁元素含量的比较（±S，ng/g，各组n=15）

Table5、ComparedwiththeelementofCr、Ni、FeinthepointofJianliaobetweentwogroups铬Cr镍Ni铁Fe实验组（电针）303.93884±115.7134.77991±64.5514175.591±5327.276(Electroacupuncture)对照组Control58.014030±19.395.3104262±4.8245414.2764±2531.767Comparedwiththecontrolgroup（与对照组比较）:P＜0.001实验3

结论

针行方便揿针针刺穴位组织（能够增加离子、微量元素）具有电化学原电池效应。Experiment2