水泥轻舟的制作方法

1、水泥轻舟水泥轻舟轻舟之父轻舟之父Clyde Kesler 一、外形设计速度为速度为4m/s时摩擦阻力大约时摩擦阻力大约65.46N，由水的粘滞力造成的阻力约为，由水的粘滞力造成的阻力约为89.80N 二、混凝土设计二、混凝土设计设计目标：设计出强度大于设计目标：设计出强度大于50MPa，抗折强度大于，抗折强度大于10Mpa的无坍落度的膏状细石混凝土，采用纤维增强。的无坍落度的膏状细石混凝土，采用纤维增强。1 、原材料、原材料1.1 水泥实验采用葛洲坝三峡牌P.O 42.5普通硅酸盐水泥序号检测项目PO42.5水泥标准指标检测结果1细度80m筛余(%)10.01.252标准稠度(%)29.03凝

2、结时间(h:min)初凝0:452:18终凝10:003:355抗折强度(MPa)3d3.55.228d6.49.66抗压强度(MPa)3d17.024.728d42.353.0试样试样名称名称13.29.54.752.361.180.60.30.15筛底筛底2料料7.3484.0699.49 3料料6.8693.69 98.37 巴河黄砂巴河黄砂3.312.62737.782.898.6试样试样类型类型表观密度表观密度(g/cm3)压碎值压碎值 吸水率吸水率 含泥量含泥量2料料2.6709.51.20.63料料2.7411.20.6巴河黄砂巴河黄砂 2.682根据通过率根据通过率P=100

3、0（d/D）1/n，当，当n取取0.45、0.5、0.55时，相应的合成级配如下：时，相应的合成级配如下：图图1 n=0.45时相应的合成级配曲线时相应的合成级配曲线图图2 n=0.5时相应的合成级配曲线时相应的合成级配曲线图图3 n=0.55时相应的合成级配曲线时相应的合成级配曲线类型类型水泥水泥用量用量kg/m32#kg/m33#kg/m3砂砂kg/m3外加剂外加剂kg/m3(1.5%)纤维纤维kg/m3(0.6%)水水kg/m33d强度强度/MPa7d强度强度/MPa28d强度强度/MPa抗折抗折抗压抗压抗折抗折抗压抗压抗折抗折抗压抗压粗粗480346.99520.49867.487.2

4、6.61924.2116.87.1132.288.3743.7细细480346.99520.49867.487.26.61925.9423.08.1832.848.8144.6细细600306.9460.35767.259.06.62166.5826.59.2444.2410.352.82.1罗洋粗、细纤维对比试验2.实验实验纤维纤维掺量掺量水泥水泥/ kg/m32#料料/ kg/m33#料料/ kg/m3砂砂/ kg/m3外加剂外加剂/ kg/m3(1.5%)纤维纤维/ kg/m3水水/ kg/m33d强度强度/MPa7d强度强度/MPa28d强强度度/MPa抗折抗折抗压抗压抗折抗折抗抗压压

5、抗抗折折抗抗压压0%480352.2528.3867.57.201737.9732.29.3039.710.050.20.4%480352.2528.3867.57.24.41737.7231.28.1837.19.67480.6%480352.2528.3867.57.26.61735.9422.57.4332.98.8144.60.8%480352.2528.3867.57.28.81735.2320.77.3730.08.6241.11.0%480352.2528.3867.57.2111735.4719.78.1131.78.5542.3纤维掺量纤维掺量水泥水泥/ kg/m32#料料/

6、 kg/m33#料料/ kg/m3砂砂/ kg/m3外加剂外加剂/ kg/m3(1.5%)纤维纤维/ kg/m3水水/ kg/m33d强度强度/MPa7d强度强度/MPa28d强度强度/MPa抗折抗折抗压抗压抗折抗折抗抗压压抗折抗折抗压抗压0%600319.7479.6799.3901928.5346.610.455.811.1560.370.04%600319.7479.6799.390.441929.2245.59.7752.411.4865.720.08%600319.7479.6799.390.881929.5246.410.657.212.5470.570.12%600319.747

7、9.6799.391.321928.7243.69.754.311.4362.530.16%600319.7479.6799.391.761928.4742.09.7855.412.0264.020.20%600319.7479.6799.392.21928.239.69.0650.610.5163.030.4%600306.9460.4767.394.42167.4924.28.4339.29.3449.10.6%600306.9460.4767.396.62166.5826.49.2544.210.352.80.8%600306.9460.4767.398.82165.8518.97.7133.08.3643.51.0%600306.9460.4767.39112165.5719.67.7336.28.4046.8三、三、摸具制作摸具制作肋板制作 船体拼接龙骨制作 1、肋板制作肋板制作四、船体成型五、五、图案设计图案设计四、四、下水