1145合金铝箔英文版企业标准

1、technical data sheet aluminium foil version: 2005-12-09 supplier: alcoa shanghai aluminium product 855 jiang chuan road, minghang district shanghai 200245 china tel: 86 21 6430 1730 material: aluminum foil, including light gauge (6.30-6.5, 7, 8-9 microns) and 12-16 micra for converter foil purpose,

2、adequate for lamination, printing, lacquering as well as 20，25，30，40 micra for pharmaceutical. specifications aluminium 6.30-6.50 microns foil remarks property u.o.m * aluminum foil, for converter foil purpose, adequate for lamination lacquering, printing as well as household use. alloy 1145 - tempe

3、rsoft (o) as ordered: soft(o) other tempers on request. gaugemicrons6.30-6.50 tolerancemicrons 8% on spot measurement. 4% on average for lots bigger than 10 tons this refers to tolerances around the technical target as set on the mill when rolling. the weighing of sample of known area will be the re

4、ferred method. surface finish bright/dulldepending on order, matt or dull side wound to outside.one side bright, one side dull, up to 40m wettability grade (minimum) acvalid for temper o (soft). splices number (maximun) reel diameter mm 400600800 max splice per reel. # 246 ultrasonic welding. positi

5、on: longitudinal to spool axial. overlapping 5 mm. marked at the reel end by aluminum flags (10 x 10 mm) each side. pinholesnumber/sq.m pinholes/m2 according to en-546-4 max.300. selected area for counting pinholes must be representative of the entire surface. tensile strength mpa 50 elongation%(min

6、) 1.0 outside diameter mm for cores of 3” i.d.(76.2mm) ,min.300 mm and max 600mm. for cores of 150152.4 mm i.d., min. 400 mm and max. 800 mm. widthmm 2501340 tolerance 1 ( up to 1620 mm on customer demand) width measurement at 20-25 degrees. trace elements % pb0.01 cd0.01 as0.01 the level of the sum

7、 of cadmium, lead, mercury and hexavalent chromium is below 100 ppm. corealuminum / steel standard core extension is 5 mm for each side with no slot on it. core i.d.mm76.20.2(aluminum) / 1510.3(steel)6” cores on demand. unwinding properties max (m)1.5 m method for testing stickiness as attached . le

8、ngth of foil is necessary to cause unwind max. 1.5 m on the entire length of the coil. reel lengthm +0 / -5% of the specified length for 90% of the coils. for the remaining 10%, +0 / -20%. coil eccentricity mm width - 1290 o.d.- 400 mm34 o.d.400 x 60057 * u. o. m unit of measure. specifications alum

9、inium 7 microns. foil remark property u.o.m * aluminum foil, for converter foil purpose, adequate for lamination lacquering, printing as well as household use. alloy 1145- tempersoft (o) as ordered: soft(o) other tempers on request gaugemicrons7.0 tolerancemicrons 8% on spot measurement. 4% on avera

10、ge for lots bigger than 10 tons this refers to tolerances around the technical target as set on the mill when rolling. the weighing of sample of known area will be the referred method. surface finish bright/dulldepending on order, matt or bright side wound to out side.one side bright, one side dull,

11、 up to 40m wettability grade (minimum) acvalid for temper o (soft). splices number (maximun) reel diameter mm 400600800 max. splices per reel. # 246 ultrasonic welding. position: longitudinal to spool axial. overlapping 5 mm. marked at the reel end by aluminum flags (10 x 10 mm) each side. pinholesn

12、umber/sq.m pinholes/m2 according to en-546-4 max.200 selected area for counting pinholes must be representative of the entire surface. tensile strength mpa 50 elongation%(min) 1.0 outside diameter mm(max) for cores of 3” i.d.(76.2mm) ,min.300 mm and max 600mm. for cores of 150152.4 mm i.d., min. 400

13、 mm and max. 800 mm. widthmm 2501340 tolerance 1 ( up to 1620 mm on customer demand) width measurement at 20-25 degrees. trace elements % pb0.01 cd0.01 as0.01 the level of the sum of cadmium, lead, mercury and hexavalent chromium is below 100 ppm. corealuminum / steel standard core extension is 5 mm

14、 for each side with no slot on it. core i.d.mm76.20.2(aluminum) / 1510.3(steel)6” cores on demand. unwinding properties max (m)1.5 m method for testing stickiness as attached . length of foil is necessary to cause unwind max. 1.5 m on the entire length of the coil reel lengthm +0 / -5% of the specif

15、ied length for 90% of the coils. for the remaining 10%, +0 / -20%. eccentricitymm width - 1290 o.d.- 400 mm34 o.d.400 x 60057 u. o. m unit of measure specifications aluminium 8-9 microns. foil u.o.m *remark property aluminum foil, for converter foil purpose, adequate for lamination lacquering, print

16、ing as well as household use. alloy1145- tempero as ordered: soft (o). other tempers on request gaugemicrons8-9 tolerancemicrons 8% on spot measurement. 4% on average for lots bigger than 10 tons this refers to tolerances around the technical target as set on the mill when rolling. the weighing of s

17、ample of known area will be the referred method. surface finish bright/dull depending on order, dull or bright side wound to out side.one side bright, one side dull, up to 40m wettability grade (minimum) acvalid for temper o (soft). . splices number (maximun) reel diameter mm 400600800 max splices p

18、er reel # 246 ultrasonic welding. position: longitudinal to spool axial. overlapping 5 mm. marked at the reel end by aluminum flags (10 x 10 mm) each side. pinholesnumber/sq.m pinholes/m2 according to en-546-4 max.100 selected area for counting pinholes must be representative of the entire surface.

19、tensile strength mpa50 elongation%(min)1.0 outside diameter mm(max) for cores of 3” i.d.(76.2mm) ,min.300 mm and max 600mm. for cores of 150152.4 mm i.d., min. 400 mm and max. 800 mm. widthmm 2501340 tolerance 1 ( up to 1620 mm on customer demand) width measurement at 20-25 degrees. trace elements %

20、 pb0.01 cd0.01 as0.01 the level of the sum of cadmium, lead, mercury and hexavalent chromium is below 100 ppm. corealuminum / steel standard core extension is 5 mm for each side with no slot on it. core i.d.mm76.20.2(aluminum) / 1510.3(steel)6” cores on demand. unwinding properties max (m)1.5 m meth

21、od for testing stickiness as attached . length of foil is necessary to cause unwind max. 1.5 m on the entire length of the coil reel lengthm +0 / -5% of the specified length for 90% of the coils. for the remaining 10%, +0 / -20%. eccentricitymm width - 1290 o.d.- 400 mm34 o.d.400 x 60057 * u. o. m u

22、nit of measure specifications aluminium 12-16 microns. foil remark property u.o.m * aluminum foil, for converter foil purpose, adequate for lamination lacquering, printing as well as household use. alloy1145- tempersoft (o) as ordered: soft (o). other tempers on request. gaugemicrons12-16 tolerancem

23、icrons 8% on spot measurement. 4% on average for lots bigger than 10 tons this refers to tolerances around the technical target as set on the mill when rolling. the weighing of sample of known area will be the referred method. surface finish bright/dulldepending on order, dull or bright side wound t

24、o out side.one side bright, one side dull, up to 40m wettability grade (minimum) acvalid for temper o (soft). . splices number (maximun) reel diameter mm 400600800 max. splices per reel #235 ultrasonic welding. position: longitudinal to spool axial. overlapping 5 mm. marked at the reel end by alumin

25、um flags (10 x 10 mm) each side. pinholesnumber/sq.m pinholes/m2 according to en-546-4 max.20 selected area for counting pinholes must be representative of the entire surface. tensile strength mpa 50 elongation%(min)1.0 outside diameter mm(max) for cores of 3” i.d.(76.2mm) ,min.300 mm and max 600mm.

26、 for cores of 150152.4 mm i.d., min. 400 mm and max. 800 mm. widthmm 2501340 tolerance 1 ( up to 1620 mm on customer demand) measurement at 20-25 degrees. trace elements %pb0.01 cd0.01 as0.01 the level of the sum of cadmium, lead, mercury and hexavalent chromium is below 100 ppm. corealuminum / stee

27、l standard core extension is 5 mm for each side with no slot on it. core i.d.mm76.20.2(aluminum) / 1510.3(steel)6” cores on demand. unwinding properties max (m)1.5 m method for testing stickiness as attached . length of foil is necessary to cause unwind max. 1.5 m on the entire length of the coil re

28、el lengthm +0 / -5% of the specified length for 90% of the coils. for the remaining 10%, +0 / -20%. eccentricitymm width - 1290 o.d.- 400 mm34 o.d.400 x 60057 * u. o. m unit of measure specifications aluminium 20 microns foil remarks property u.o.m * aluminum foil, for converter foil purpose, adequa

29、te for lamination lacquering, printing as well as household use. alloy1145/8011- temperh18 as ordered: soft(o) other tempers on request. gaugemicrons20 tolerancemicrons 8% on spot measurement. 4% on average for lots bigger than 10 tons this refers to tolerances around the technical target as set on

30、the mill when rolling. the weighing of sample of known area will be the referred method. surface finish bright/dulldepending on order, matt or dull side wound to outside.one side bright, one side dull, up to 40m wettability grade (minimum) - valid for temper o (soft). splices number (maximun) reel d

31、iameter mm 400600800 max splice per reel. # 234 ultrasonic welding. position: longitudinal to spool axial. overlapping 5 mm. marked at the reel end by aluminum flags (10 x 10 mm) each side. pinholesnumber/sq.m pinholes/m2 according to en-546-4 max.3. selected area for counting pinholes must be repre

32、sentative of the entire surface. tensile strength mpa 1145:160; 8011:170 elongation%(min) 1145:0.5; 80111.0 outside diameter mm for cores of 3” i.d.(76.2mm) ,min.350 mm and max 600mm. for cores of 150152.4 mm i.d., min. 400 mm and max. 760 mm widthmm 2501450 tolerance 1 width measurement at 20-25 de

33、grees. trace elements % pb0.01 cd0.01 as0.01 the level of the sum of cadmium, lead, mercury and hexavalent chromium is below 100 ppm. corealuminum / steel standard core extension is 5 mm for each side with no slot on it. core i.d.mm76.20.2(aluminum) / 1510.3(steel)6” cores on demand. unwinding prope

34、rties max (m)1.5 m method for testing stickiness as attached . length of foil is necessary to cause unwind max. 1.5 m on the entire length of the coil. reel lengthm +0 / -5% of the specified length for 90% of the coils. for the remaining 10%, +0 / -20%. * u. o. m unit of measure. specifications alum

35、inium 25 microns foil remarks property u.o.m * aluminum foil, for converter foil purpose, adequate for lamination lacquering, printing as well as household use. alloy1145/8011- temperh18 as ordered: soft(o) other tempers on request. gaugemicrons25 tolerancemicrons 8% on spot measurement. 4% on avera

36、ge for lots bigger than 10 tons this refers to tolerances around the technical target as set on the mill when rolling. the weighing of sample of known area will be the referred method. surface finish bright/dulldepending on order, matt or dull side wound to outside.one side bright, one side dull, up

37、 to 40m wettability grade (minimum) - valid for temper o (soft). splices number (maximun) reel diameter mm 400600800 max splice per reel. # 123 ultrasonic welding. position: longitudinal to spool axial. overlapping 5 mm. marked at the reel end by aluminum flags (10 x 10 mm) each side. pinholesnumber

38、/sq.m pinholes/m2 according to en-546-4 no pinholes selected area for counting pinholes must be representative of the entire surface. tensile strength mpa 1145:160; 8011:170 elongation%(min) 1145:0.5; 80111.0 outside diameter mm for cores of 3” i.d.(76.2mm) ,min.350 mm and max 600mm. for cores of 15

39、0152.4 mm i.d., min. 400 mm and max. 760 mm widthmm 2501450 tolerance 1 width measurement at 20-25 degrees. trace elements % pb0.01 cd0.01 as0.01 the level of the sum of cadmium, lead, mercury and hexavalent chromium is below 100 ppm. corealuminum / steel standard core extension is 5 mm for each sid

40、e with no slot on it. core i.d.mm76.20.2(aluminum) / 1510.3(steel)6” cores on demand. unwinding properties max (m)1.5 m method for testing stickiness as attached . length of foil is necessary to cause unwind max. 1.5 m on the entire length of the coil. reel lengthm +0 / -5% of the specified length f

41、or 90% of the coils. for the remaining 10%, +0 / -20%. * u. o. m unit of measure. specifications aluminium 30 microns foil remarks property u.o.m * aluminum foil, for converter foil purpose, adequate for lamination lacquering, printing as well as household use. alloy8011- tempero as ordered: soft(o)

42、 other tempers on request. gaugemicrons30 tolerancemicrons 8% on spot measurement. 4% on average for lots bigger than 10 tons this refers to tolerances around the technical target as set on the mill when rolling. the weighing of sample of known area will be the referred method. surface finish bright

43、/dulldepending on order, matt or dull side wound to outside.one side bright, one side dull, up to 40m wettability grade (minimum) a valid for temper o (soft). splices number (maximun) reel diameter mm 400600800 max splice per reel. # 012 ultrasonic welding. position: longitudinal to spool axial. ove

44、rlapping 5 mm. marked at the reel end by aluminum flags (10 x 10 mm) each side. pinholesnumber/sq.m pinholes/m2 according to en-546-4 no pinholes selected area for counting pinholes must be representative of the entire surface. tensile strength mpa60 elongation%(min)2.0 outside diameter mm for cores

45、 of 3” i.d.(76.2mm) ,min.350 mm and max 600mm. for cores of 150152.4 mm i.d., min. 400 mm and max. 760 mm widthmm 2501450 tolerance 1 width measurement at 20-25 degrees. trace elements % pb0.01 cd0.01 as0.01 the level of the sum of cadmium, lead, mercury and hexavalent chromium is below 100 ppm. cor

46、ealuminum / steel standard core extension is 5 mm for each side with no slot on it. core i.d.mm76.20.2(aluminum) / 1510.3(steel)6” cores on demand. unwinding properties max (m)1.5 m method for testing stickiness as attached . length of foil is necessary to cause unwind max. 1.5 m on the entire lengt

47、h of the coil. reel lengthm +0 / -5% of the specified length for 90% of the coils. for the remaining 10%, +0 / -20%. * u. o. m unit of measure. specifications aluminium 40 microns foil remarks property u.o.m * aluminum foil, for converter foil purpose, adequate for lamination lacquering, printing as

48、 well as household use. alloy8011- tempero as ordered: soft(o) other tempers on request. gaugemicrons40 tolerancemicrons 8% on spot measurement. 4% on average for lots bigger than 10 tons this refers to tolerances around the technical target as set on the mill when rolling. the weighing of sample of

49、 known area will be the referred method. surface finish bright/dulldepending on order, matt or dull side wound to outside.one side bright, one side dull, up to 40m wettability grade (minimum) a valid for temper o (soft). splices number (maximun) reel diameter mm 400600800 max splice per reel. # 012

50、ultrasonic welding. position: longitudinal to spool axial. overlapping 5 mm. marked at the reel end by aluminum flags (10 x 10 mm) each side. pinholesnumber/sq.m pinholes/m2 according to en-546-4 no pinholes selected area for counting pinholes must be representative of the entire surface. tensile st

51、rength mpa60 elongation%(min)2.0 outside diameter mm for cores of 3” i.d.(76.2mm) ,min.350 mm and max 600mm. for cores of 150152.4 mm i.d., min. 400 mm and max. 760 mm widthmm 8001450 tolerance 1 width measurement at 20-25 degrees. trace elements % pb0.01 cd0.01 as0.01 the level of the sum of cadmiu

52、m, lead, mercury and hexavalent chromium is below 100 ppm. corealuminum / steel standard core extension is 5 mm for each side with no slot on it. core i.d.mm76.20.2(aluminum) / 1510.3(steel)6” cores on demand. unwinding properties max (m)1.5 m method for testing stickiness as attached . length of fo

53、il is necessary to cause unwind max. 1.5 m on the entire length of the coil. reel lengthm +0 / -5% of the specified length for 90% of the coils. for the remaining 10%, +0 / -20%. * u. o. m unit of measure. quality record specifications each shipment for each shipment alcoa shanghai shall send separa

54、tely a quality record with the following information: -.company name - order number - customer order number - customer material number - date of shipment - ordered thickness - ordered width each reel for each reel listed in the record: - reel id number - net weight - thickness- alloy - width disposi

55、tion of defective foil - incoming shipments are to be examined before unloading. when damaged rolls are discovered, if carrier is responsible, notation is made on freight bill before material is removed, and signed by driver and receiver. if rolls are intact and show no sign of rough handling by car

56、rier, but still appear to have damage, the condition should be reported immediately to the shipping plant for disposition; - rejected metal, when returned, must have the foil roll identification ticket attached; - when possible, samples showing the problem should be attached to the roll and forwarde

57、d to supplier; - detection and complaint shall be made to the producing plant within 90 days of receipt of foil, except in the case of corrosion when the time limit is 60 days; - supplier has the right to make an inspection of the rejected foil prior to authorizing a return. packing specifications q

58、uantities - as specified on the purchase order with a tolerance of 10% unless otherwise stated on the order. packaging - foil rolls are to be suspended in steel racks or in wooden boxes and shall be packed in such a manner that normal handling by common carrier will ensure safe transportation withou

59、t damage to foil. this includes wrapping to protect foil from water stain and corrosion identification - each rack or box in a shipment shall have its own unique identification number clearly visible from both ends of rack or box. further, each rack or box and each individual roll shall be identifie

60、d with the following: a.order number (release no.) b.part number c.gauge (mm) d.width (mm) e.net weight (kgs) f.number of splices g. alloy, temper. h.roll identification number (traceable to source, or point at which composition was determined) porosity in foil rolling 1. terms and definitions for t