钢材抗拉强度与硬度对照表

依据德国尺度DIN50150,以下是常常使用范围的钢材抗拉强度与维氏硬度、布氏硬度、洛氏硬度的比较表。之勘阻及广创作抗拉强度维氏硬度布氏硬度洛氏硬度RmHVHBHRCN/mm22508076.0-2708580.7-2859085.2-3059590.2-32010095.0-33510599.8-350110105-370115109-380120114-400125119-415130124-430135128-450140133-465145138-480150143-490155147-510160152-530165156-545170162-560175166-575180171-595185176-610190181-625195185-640200190-660205195-675210199-690215204-705220209-720225214-740230219-755235223-77024022820.378524523321.380025023822.282025524223.183526024724.085026525224.886527025725.688027526126.490028026627.191528527127.893029027628.595029528029.296530028529.899531029531.0103032030432.2106033031433.3109534032334.4112535033335.5111536034236.6119037035237.7122038036138.8125539037139.8129040038040.8132041039041.8135042039942.7138543040943.6142044041844.5145545042845.3148546043746.1152047044746.91555480(456)47.71595490(466)48.41630500(475)49.11665510(485)49.81700520(494)50.51740530(504)51.11775540(513)51.71810550(523)52.31845560(532)53.01880570(542)53.61920580(551)54.11955590(561)54.71995600(570)55.22030610(580)55.72070620(589)56.32105630(599)56.82145640(608)57.32180650(618)57.866058.367058.868059.269059.770060.172061.074061.876062.578063.380064.082064.784065.386065.988066.490067.092067.5940HB有两种一种是ＨＢＳ（钢球）另一种是ＨＢＷ（硬质合金球）用必定直径的钢球或硬质合金球，以规定的试验力（F）压入式样概略，经规定坚持时间后卸除试验力，测量试样概略的压痕直径L）。布氏硬度值是以试验力除以压痕球形概略积所得的商。以HBS（钢球）示意，单位为N/mm2(MPa)。其计算公式为：式中：F--压入金属试样概略的试验力，N；D--试验用钢球直径，mm；d--压痕均匀直径，mm。测定布氏硬度较正确靠谱，但一般HBS只合用于450N/mm2（MPa）以下的金属资料，关于较硬的钢或较薄的板材不合用。在钢管尺度中，布氏硬度用途最广，常常以压痕直径d来示意该资料的硬度，既直观，又方便。布氏硬度试验还可用于有色金属和软钢，采纳小直径球压头能够测量小尺寸和较绵力料。布氏硬度计多用于原资料和半成品的检测，因为压痕较大，一般不用于成品检测。举例：120HBS10/1000/30：示意用直径10mm钢球在1000Kgf（9.807KN）试验力作用下，坚持30s（秒）测得的布氏硬度值为120N/mm2（MP