镁铝合金表面处理简介

1、镁铝合金表面处理简介Introduce the Surface Processing of the Alloy of Magnesium and Aluminum· 镁铝合金材质特性· Characteristic of the alloy of MG and AL镁是一种非常活泼之元素，相对的其材质本身亦非常易生锈蚀，因此必须仰赖表面处理来保护其本身之材质。MG is an active element ,it is more rustied than others. So it must depend on surface processing to protect i

2、t.· 金属材质表面处理项目· Item of mental surface processing 1.铬系皮膜处理与涂装Phosphating filming and coating of chromium series2.非铬系皮膜处理与涂装Phosphating filming and coating of not chromium series 3.电镀镍处理Electroplated nickel processing4.电镀铬处理Electroplated chromium processing5.电镀18K金处理Electroplated 18K gold p

3、rocessing6.阳极处理与染色Plating and dyeing镁铝合金表面处理项目之说明与检验方式Instruction the Surface Processing of the Alloy of Magnesium and Aluminum and check mode1.铬系皮膜处理Phosphating filming of chromium seriesa.说明 instruction：（1）铬系皮膜处理是目前最为普遍处理之方式亦为最安定、最成熟之处理方式，惟其原料特性具毒性，因此在未来几年内会禁止使用。其流程请参考图表。Phosphating filming of chr

4、omium series is the most universal process manner, also is the most stable and mature. Only does its materials have poison , it will be forbid to use. Its process flow refer to the diagram.（2）注意事项：注若需要表面涂装时，请务必注意其涂装制程是否有破坏到其表面之皮膜层，因其表面皮膜层最重要的是防止锈蚀，而其最重要的是当作镁合金与涂料之介质使密着性会更好，因此涂装时不能有破坏皮膜之现象发生。Remarks:

5、 If the surface need coating , please be sure to notice if the coating process damage the surface film. Because the surface film the most important is prevent to rustingb.检验方式check manner：（1）电阻值：皮膜表面其电阻值，以三用电表检测之。, examined by three-purpose galvanometer.（2）涂装密着性：指皮膜处理后，再涂装、以有格刮刀分割为100格并以3M610胶带测试98%

6、以上，不能有剥落现象。Coating adhesion: it will not peel off coating again then cut 100 cross with a scraper and check 98% products with 3M610 adhesive tape after phosphating filming.（3）耐蚀性：以盐雾测试机检测皮膜层与涂装层，最基本皮膜层必须超过24小时98%无腐蚀现象，而涂装层则必须超过96小时以上98%无腐蚀现象，才视之为合格。Corrosion resistance:2.非铬系皮膜处理与涂装Phosphating filmin

7、g and coating of not chromium series其特性与铬系是类似的，除了具有非毒性外其检验方式与处理方式皆与铬系相同，因此请参考铬即可。The characteristic is similar with chromium series ; besides it is poisonous the manner of inspection and phosphating filming is the same with chromium series . so please refer to chromium .a.说明instruction：此项处理为最新发展之处理，

8、目前只有美国方面发展出来，电镀材料本公司亦于83年12月完成配方，其特性是导电性非常好，电阻值可小于以下，并具有耐蚀性。Phosphating filming and coating of not chromium series is the newest process , now it is developed by America,the electroplate company finished the formula in December in 1983 ,its characteristic is having better electric conductivity,the ,

9、and it is corrosion-resistant.b.检验方式check manner：（1）电阻值：镀层表面电阻值以精密电表测之。, examined by accurate galvanometer.（2）密着性：以有格刮刀分割为100格，并以3M610胶带测试，不得有剥落现象产生。Adhersion: it will not peel off coating then cut 100 cross with a scraper and check with 3M610 adhesive tape.（3）耐蚀性：以盐雾测试机检测镀层，其至少要24小时以上盐雾测试通过，才视之为合格。

10、Corrosion resistance:check cladding material with salt test machine , the test pass at least 24 hours later , then it is qualified .· 电镀铬处理Electroplated chromium processinga.说明：此项处理，是在电镀镍上面加上一层镀铬处理，可使镁合金镀件更加亮丽、美观。a. instruction:the process is adding a tier of electroplated chromium on the elect

11、roplated nickel, it will make the electroplate of Mg alloy more gorgeous and more beautiful .b.检验方式：与电镀镍相同。b. check manner : the same as electroplated nickels· 电镀18K金处理Electroplated 18K gold processinga.说明：此项处理，是在电镀镍上面加上一层镀铬处理，可使镁合金镀件更有价值感。a. instruction :the process is adding a tier of electro

12、plated chromium on the electroplated nickel, it will make the electroplate of Mg alloy more valuable .b.检验方式：与电镀镍相同。b. check manner : the same as electroplated nickels· 阳极处理与染色Plating and dyeinga.说明：镁合金阳极处理其处理方式与铝合金相似，只是药水配方与整流器电流强度略有不同，此项处理目的在于防止锈蚀，但是不能导电，是属于非导电之皮膜处理。a. instruction:the process

13、ing of Mg alloy plating is similar with Al alloys , only are medicinal liquid prescription and commutators current intensity a little different. The purpose of this processing is to prevent rusting .It belong to non-electric conduction phosphating filming because it can not conduct electricity.b.检验方

14、式：check manner（1）染色密着性：以有格刮刀分割为100格并以3M610胶带测试，98%以上不能有剥落现象。Dyeing adhesion: it will not peel off colors when cut 100 cross with a scraper and check 98% products with 3M610 adhesive tape after dyed.（2）耐蚀性：阳极处理之盐雾测试，可依客户要求来规定，但至少要有24小时以上，视产品之定之。Corrosion resistance: salt test of plating , maybe accor

15、ding to the customers needs , depend on the production , but at least 24 hours .镁合金外壳表面处理流程图进 料 incoming materials1. 进料检验作业说明 2.进料检验表检验标准表1. incoming materials check operation instruction2. incoming materials check report3. AQL check standard report铬 酸 Chromium acid1. 药水检验表 2.制程广告牌 3.出货作业说明书检验标准表1.

16、medicial liquids check report 2.process signboard3.outgoing products operation booklet 4.AQL check standard report烤漆进料incoming baked paint1. 进料检验作业说明书 2.进料检验表检验标准表1.incoming materials check operation instruction2.incoming materials check report3.AQL check standard report底 漆 primer1. 制程广告牌 2.底漆外观检查1.

17、 process signboard 2.primer appearance inspection补 土 repair/mend    1.制程广告牌 process signboard底 漆 primer1.制程广告牌 process signboard美工线designing line1. 制程广告牌 2.底漆外观第一次细部修补1.process signboard 2.primer appearance first touch-up of details 面 漆 silver1. 制程广告牌 2.面漆外观检查1.process signboard 2.silv