《喷涂速凝高分子液体橡胶防水胶膜应用技术规程》

ICS号中国标准文献分类号中国城市科学研究会标准T/CSUSXX-202X喷涂速凝高分子液体橡胶防水胶膜应用技术规程Applicationtechnicalregulationsofsprayingquick-settingpolymerliquidrubberwaterproofingmembrane（征求意见稿）XXXX-XX-XX发布XXXX-XX-XX实施中国城市科学研究会发布目次1总则···························································································22术语·························································································33基本规定····················································································44材料···················································································55设计···················································································85.1一般规定················································································85.2屋面防水工程···································································85.3地下防水工程···································································125.4地铁及隧道防水工程···································································156施工···················································································196.1一般规定···············································································196.2基层处理···································································196.3施工准备···································································206.4喷涂施工···································································206.5搭接和甩槎的操作方法································································216.6保护层施工···································································227工程验收···················································································237.1一般规定···············································································237.2主控项目···································································247.3一般项目···································································258安全和环境保护············································································268.1成品保护···············································································268.2安全注意事项···································································26附录A喷涂速凝高分子液体橡胶防水胶膜A组分现场检验方法···············27附录B喷涂速凝高分子液体橡胶防水胶膜制备方法···············28本标准用词说明····························································29引用标准名录·····················································································301总则为规范喷涂速凝高分子液体橡胶防水胶膜的设计、施工及工程验收，保证工程质量，实现高质量发展及满足国家环保节能要求和规范施工做法，制定本标准。本标准适用于市政及建筑防水工程。可应用于地铁车站、隧道、污水处理厂、垃圾填埋场、公路、桥梁，还可应用于铁路桥面、化工、水利、尾矿库抗渗、海港码头、管理设施及等防腐蚀、防渗漏工程。喷涂速凝高分子液体橡胶防水胶膜的设计、施工及验收除应符合本标准外，尚应符合国家、行业和地方现行有关规范和标准的规定。

2术语喷涂速凝高分子液体橡胶防水胶膜技术系统technicalsystemofpremiumliquidrubber是由喷涂速凝高分子液体橡胶防水胶膜、专用喷涂设备和喷涂方法完成防水功能的系统。喷涂速凝高分子液体橡胶防水胶膜sprayingrapid-setsyntheticliquidrubberwaterproofingmembrane喷涂速凝高分子液体橡胶防水胶膜是由合成高分子聚合物和超细、悬浮、微乳型改性乳化沥青为主要材料，以水为介质，并添加助剂，经加工制成A、B组分，经专用设备喷涂，快速固化为防水橡胶层。具有无污染、易操作、高弹性、耐老化的特点。喷涂速凝高分子液体橡胶防水胶膜A组分partAofsprayingrapid-setsyntheticliquidrubberwaterproofingmembraneA组分是由合成高分子聚合物和超细、悬浮、微乳型改性乳化沥青构成的混合物。喷涂速凝高分子液体橡胶防水胶膜B组分partBofsprayingliquidrubberB组分是由一定浓度的轻金属盐构成的水溶液。专用喷涂设备specialsprayingequipment专用喷涂设备是由一个发动机带动的双泵、双管、双枪、双路进、回流管组成的喷涂设备。喷涂方法sprayingmethod将A组分和B组分分别置于两个不同的容器中，启动专用喷涂设备的发动机，带动两个低压高流量流体泵，扣动控制两管喷枪的扳机，A组分和B组分同时喷出交合，瞬时反应，一次，数遍，横竖交叉喷涂，不需要间歇，落在待喷涂的物体上形成有一定厚度的胶膜。喷涂速凝高分子液体橡胶防水胶膜适用基底applicablesubstrate喷涂速凝高分子液体橡胶防水胶膜适用的基底：是指由混凝土、金属、木头、砖瓦、石棉瓦、土、沙和石头、塑料、玻璃、布及各种卷材与防水粘接的基础。喷涂速凝高分子液体橡胶防水胶膜加强层reinforcementlayer采用无纺布、土工布或丙纶布，裁剪至合适的尺寸，使用喷涂速凝高分子液体橡胶防水胶膜A组份浸渍或空铺，铺贴在基层上用以提高局部胶膜的抗拉强度和改善其延伸率的措施构造。

3基本规定根据建筑物的性质、重要程度、防水设防等级、使用功能等，选择适宜的喷涂胶膜厚度。喷涂速凝高分子液体橡胶防水胶膜为“皮肤式”防水技术系统，胶膜与基底不窜水、不剥离，设计可采用单层防水设计。本防水胶膜单层使用时其防水胶膜设计厚度不应小于2.4mm。本防水胶膜作为一道防水层时厚度为1.5mm。建筑与市政工程设计及工程防水做法应依据工程防水等级和工程类别确定，符合GB55030并应按3.0.2表选用。表3.0.2工程防水等级和工程类别单位为：mm防水等级工程类别屋面工程地下工程建筑外墙建筑室内道桥及蓄水工程地铁隧道I级1.5+II级1.5-喷涂速凝高分子液体橡胶防水胶膜防水工程应根据工程的使用环境及胶膜的耐候性，选择合适的保护措施。喷涂速凝高分子液体橡胶防水胶膜防水工程所采用的材料之间应具有相容性。

4材料喷涂速凝高分子液体橡胶防水胶膜、涂刷型橡胶沥青防水涂料应进行进场检验，并符合下列规定：喷涂速凝高分子液体橡胶防水胶膜的性能要求和试验方法应符合表4.0.1的规定。表4.0.1喷涂速凝高分子液体橡胶防水胶膜的性能指标和试验方法序号项目指标试验方法I型II型固体含量/％≥5555GB/T16777凝胶时间/s≤55GB/T23446平均粒径/um≤33GB/T19077实干时间/h≤88GB/T16777耐热度（120±2）℃（140±2）℃GB/T16777无流淌、滑动、滴落GB/T16777不透水性0.3MPa，120min不透水GB/T16777耐水性（23℃×14d）无裂纹、分层、起泡和破碎GB/T1690粘结强度/MPa≥干燥基面0.400.60GB/T16777潮湿基面0.400.60浸水处理后保持率0.400.50弹性恢复率/%≥8590GB/T23457钉杆自愈性无渗水GB23441吸水率（24h）/%≤2.0GB/T19250低温柔性无处理-20℃，无裂纹-30℃，无裂纹GB/T16777热处理-18℃，无裂纹、断裂-28℃，无裂纹、断裂酸处理-15℃，无裂纹、断裂-25℃，无裂纹、断裂碱处理盐处理紫外线处理拉伸性能拉伸强度/MPa≥无处理0.600.8GB/T528断裂伸长率/%≥无处理1000碱处理800酸处理盐处理热处理紫外线处理注：根据特定项目，供需双方可以商定具体技术指标。涂速凝高分子液体橡胶防水胶膜A、B组分外观要求应符合表4.0.2的规定。表4.0.2喷涂速凝液体橡胶A、B组分外观要求项目A组分B组分色泽深褐色乳白色组织状态乳液（允许有析出物）固体杂质无无不正常气味无无A组分的环保指标须符合有害物质含量应符合JC1066《建筑防水涂料中有害物质限量》水性防水涂料A类的要求，见表4.0.3。表4.0.3环保性能指标项目有害物质限量试验方法总挥发性有机化合物（g/L）≤80GB/T41078水性涂料游离甲醛/mg/kg≤100苯、甲苯、乙苯和二甲苯总和/mg/kg≤300氨/mg/kg≤500节点处理用胎体增强材料宜选用符合《屋面工程技术规范》GB50345附录B.1.9要求的材料。喷涂速凝高分子液体橡胶防水胶膜与其它材料复合使用时，应符合下列规定：1相邻材料之间应相容。不相容材料复合使用时，中间应设置隔离层，且隔离层材料与相邻材料均应有良好的相容性；2喷涂速凝高分子液体橡胶防水胶膜的上部不得与采用有机化学溶剂涂料、热熔法施工的防水卷材直接复合。运输、储存1喷涂速凝高分子液体橡胶防水胶膜应密闭包装，容器表面应标明名称、生产厂家、执行标准、生产日期和产品的有效期。2喷涂速凝高分子液体橡胶防水胶膜的储存和运输应密闭保存，避免雨淋和暴晒，现场存放应整齐并应严格控制物料温度在5℃～35℃之间，冬季应采取保温措施，夏季应存放在阴凉干燥处或采取防晒措施。

5设计5.1一般规定喷涂速凝高分子液体橡胶防水胶膜的防水设计应包括下列内容：1防水工程的设防等级和设防要求；2喷涂速凝高分子液体橡胶防水胶膜性能及应用要求；3节点及细部构造防水设计；4防水胶膜应有保护措施。喷涂速凝高分子液体橡胶防水胶膜应设置在防水工程结构的迎水面1防水工程的设防等级和设防要求；2喷涂速凝高分子液体橡胶防水胶膜性能及应用要求；3节点及细部构造防水设计；4防水胶膜应有保护措施。5.2屋面防水工程屋面防水工程，喷涂速凝高分子液体橡胶防水胶膜采用单独使用时，设计厚度应符合3.0.1的要求；与其他材料复合使用时，设计厚度不宜小于1.5mm，并符合GB55030的规定。屋面隔离层材料宜选用100g/m²无纺布、或0.4mm以上的聚乙烯、聚丙烯膜等。结构的阴、阳角部位宜处理成圆弧状，阴角直径宜大于50mm、阳角直径宜大于10mm，并设置加强层，见图5.2.3-1和图5.2.3-2。图5.2.3-1阴角处理示意图1-基层2-加强层3-喷涂速凝高分子液体橡胶防水胶膜图5.2.3-2阳角处理示意图1-基层2-加强层3--喷涂速凝高分子液体橡胶防水胶膜喷涂速凝高分子液体橡胶防水胶膜在檐口部位收头，收头处逐渐喷薄处理或用密封胶进行密封，无组织排水檐口的防水胶膜应喷涂至檐口边缘，见图5.2.4。图5.2.4檐口防水构造示意图1-找坡层2-喷涂速凝高分子液体橡胶防水胶膜3-保护层天沟和檐沟与屋面的交接部位应设置增强层，喷涂速凝高分子液体橡胶防水胶膜应由沟底翻上至沟外侧顶部。收头处做逐渐喷薄处理或用密封胶进行密封，见图5.2.5。图5.2.5檐沟防水构造示意图1-结构层2-加强层3-喷涂速凝高分子液体橡胶防水胶膜4-保护层低女儿墙应增设防水加强层，泛水处的防水胶膜可直接喷涂至压顶下，并做铝合金压条固定，见图5.2.6。图5.2.6低女儿墙防水构造示意图1-结构层2-加强层3-喷涂速凝高分子液体橡胶胶膜高女儿墙应设加强层，防水胶膜的泛水高度不应小于250mm，泛水上部的墙体应做防水处理，并做铝合金压条固定，见图5.2.7。图5.2.7高女儿墙防水构造示意图1-结构层2-加强层3-喷涂速凝高分子液体橡胶胶膜屋面变形缝中应嵌填密封材料同时增设胎体增强材料的加强层，顶部应加混凝土或金属盖板，其防水构造见5.2.8。图5.2.8屋面变形缝防水构造示意图1-填充材料2-加强层3-聚乙烯泡沫棒4-加强层5-喷涂速凝高分子液体橡胶胶膜高低跨屋面防水层与立墙交接处变形缝，应增设夹铺胎体增强材料的加强层，缝中嵌填密封材料，并采取能适应变形的覆盖处理。防水构造见图5.2.9。图5.2.9高低跨变形缝防水构造示意图1-结构层2-加强层3-喷涂速凝高分子液体橡胶胶膜4-泛水板水落口周边500mm范围内坡度不应小于5%，防水层下应增设加强层，防水层和加强层应伸入水落口内50mm。其防水构造见图5.2.10。图5.2.10水落口防水构造示意图1-结构层2-加强层3-喷涂速凝高分子液体橡胶胶膜出屋面管道应增设加强层，周围应抹出倒角，泛水处防水层高度不应小于250mm，收头处做逐渐喷薄处理。防水构造见图5.2.11。图5.2.11出屋面管道防水构造示意图1-结构层2-加强层3-喷涂速凝高分子液体橡胶胶膜5.3地下防水工程地下防水工程中，采用喷涂速凝高分子液体橡胶防水胶膜作为防水层时，防水层应设在迎水面。喷涂速凝高分子液体橡胶防水胶膜采用单独使用时，设计厚度应符合3.0.1的要求；与其他材料复合使用时，设计厚度不宜小于1.5mm，并符合GB55030的规定。底板与立墙施工防水层连接部位甩槎与接茬构造见图5.3.3-1、图5.3.3-2和图5.3.3-3。图5.3.3-1甩槎 图5.3.3-2接槎垫层2-喷涂速凝高分子液体橡胶胶膜3-底板结构层 1-垫层2-喷涂速凝高分子液体橡胶胶膜3-地板结构层图5.3.3-3接槎1-垫层2-喷涂速凝高分子液体橡胶防水胶膜3-底板结构层地下工程混凝土施工缝采用喷涂速凝橡胶沥青防水胶膜作防水层时，应采用胎体增强层对施工缝先进行加强处理，增强层在施工缝两侧向外延伸的宽度不应小于250mm，防水构造见图5.3.4。图5.3.4施工缝防水构造示意图1-结构层2-加强层3-喷涂速凝高分子液体橡胶胶膜地下工程底板、顶板、侧墙变形缝采用喷涂速凝高分子液体橡胶防水胶膜做防水层时，变形缝两侧应做增强层，增强层向外延伸宽度不应小于250mm，防水构造见图5.3.5-1和图5.3.5-2。图5.3.5-1底板变形缝防水构造示意图1-垫层2-喷涂速凝高分子液体橡胶防水胶膜3-结构底板图5.3.5-2顶板及侧墙变形缝防水构造示意图1-结构层2-加强层3喷涂速凝高分子液体橡胶防水胶膜地下工程混凝土结构后浇带接缝处喷涂速凝高分子液体橡胶防水胶膜应设置加强层，加强层两边均应不小于250mm。防水构造见图5.3.6-1和图5.3.6-2。图5.3.6-1顶板及侧墙后浇带防水构造示意图1-结构顶板2-加强层3-喷涂速凝高分子液体橡胶防水胶膜图5.3.6-2底板后浇带防水构造示意图1-喷涂速凝高分子液体橡胶防水胶膜2-加强层3-结构底板桩头的防水层应紧密连接，并与作为加强层的喷涂速凝高分子液体橡胶防水胶膜连接成整体。防水层应做到桩头根部，喷涂时应对桩头、钢筋做遮挡保护处理，见图5.3.7。图5.3.7桩头防水构造示意图1-结构层2-喷涂速凝高分子液体橡胶防水胶膜3-加强层4-水泥基渗透结晶型防水涂料5-遇水膨胀止水胶（环）5.4地铁及隧道防水工程隧道防水工程采取对二衬结构全部包裹的防水方式，喷涂施工前应对喷混凝土表面采用砂浆找平层，或铺贴土工膜。喷涂速凝高分子液体橡胶防水胶膜采用单独使用时，设计厚度应符合3.0.1的要求；与其他材料复合使用时，设计厚度不宜小于1.5mm，并符合GB55030的规定。暗挖隧道防水构造见图5.4.3；图5.4.3暗挖隧道防水构造示意图1-二次衬砌2-喷涂速凝高分子液体橡胶胶膜3-土工膜4-初期支护暗挖隧道顶（拱）板侧墙变形缝防水构造见图5.4.3。图5.4.3暗挖隧道顶（拱）板侧墙变形缝防水构造示意图1-HDPE膜2-加强层3-喷涂速凝高分子液体橡胶胶膜4-结构层暗挖隧道结构底板变形缝防水构造见图5.4.4。图5.4.4暗挖隧道结构底板变形缝防水构造示意图1-底板结构2-喷涂速凝高分子液体橡胶胶膜3-HDPE膜4-垫层明挖结构防水构造见图5.4.5-1和图5.4.5-2图5.4.5-1明挖结构防水构造示意图1-底板2-喷涂速凝橡胶沥青防水涂料3-HDPE膜4-垫层5-喷涂速凝橡胶沥青防水涂料6-顶板7-侧墙8-喷涂速凝高分子液体橡胶胶膜9-HDPE膜10-围护结构图5.4.5-2明挖结构防水构造示意图1-拱墙2-喷涂速凝橡胶沥青防水涂料3-垫层4-HDPE膜5-喷涂速凝高分子液体橡胶胶膜6-底板

6施工6.1一般规定施工单位应具备相应的专业施工资质。喷涂作业人员应经过专门喷涂施工培训后，才能进行操作。材料进场时，喷涂速凝高分子液体橡胶防水胶膜应有：出厂检验报告、合格证和性能检测报告。材料进场后进行材料见证检验，合格后方可使用。施工前应对图纸进行会审，并按设计及工程要求，编制专项防水施工方案，经工程总包单位及监理单位审批后执行。施工时应对易受施工影响的作业区进行遮挡，施工时不得污染已完工的其他工序作业面及饰面。基层必须符合防水施工的要求，如不符合要求，则应进行处理，经过验收合格，方可进行防水施工。细部构造部位应按设计要求进行加强处理，处理措施应符合本规程第5章的要求。防水施工过程中，对工程质量应建立各道工序的自检、并设专职人员巡视检查制度。每道工序检验合格后方可进行下道工序。喷涂速凝高分子液体橡胶防水胶膜施工完毕后，检查防水层是否有漏喷、针孔、鼓泡、剥落及损伤等缺陷，并进行修补处理。喷涂速凝高分子液体橡胶喷涂施工时，以专用喷涂设备为基点，应遵循下列原则：1基层为底（顶）板时，应遵循自远而近的原则；2基层为立面时，应遵循自下而上的原则；3基层为斜面时，应遵循自低而高的原则；4基层为顶面时，应遵循自远而近的原则。喷涂速凝高分子液体橡胶防水胶膜施工应符合下列规定：1施工人员应按规定佩戴、使用安全防护用品；2屋面施工时，屋面周边和预留孔洞应设置安全防护栏和安全网或其他防止坠落措施；3施工环境温度宜为5℃～40℃。雨天、雪天、五级风以上天气不宜实施露天喷涂作业；4冬季施工应对A组分和B组分采取保温措施。6.2基层处理基层可以潮湿，但须干净、坚实、无明水，表面平整度应符合相关规范要求。各种预埋管件、设备基础、预留洞口等均应在防水层施工前埋设和安装牢固，并验收合格。所有阴角处须抹成八字角。6.3施工准备材料准备 喷涂速凝高分子液体橡胶防水胶膜由A组份和B组份组成。喷涂前使用搅拌器对A组份进行充分搅拌，搅拌方法见厂家产品说明书，将B组份在配料桶内按照比例配置好，待用。设备与机具1施工主设备：专用喷涂机、高压软管、喷枪及配套设备；2其他机具：搅拌器，配料桶、金属过滤网、工具箱等；3辅助材料：常用清理及抹灰工具，水桶，扫帚，剪刀等；4防护设备：防护服，安全帽，护目镜，安全带、乳胶手套等。喷涂设备调试应符合下列规定，合格后方可施工；1启动前连接高压软管和喷枪，并检查汽油、是否达到规定的油面，泵体阀门开关是否在关闭状态：2启动发动机处于怠速状态，检查发动机工作是否正常，确保各连接装置无渗（滴）漏；3开启阀门开关，在调试桶内调试喷枪喷涂流量，检查有无堵塞和不畅；4正式喷涂施工前应进行试喷，将喷涂料喷涂在硬纸板上，调整喷涂距离，观察涂层固化是否正常，合格后正式喷涂；5喷涂施工作业完毕，应清理喷涂设备，确认清洗干净后关机；6剩余物理应集中收集，妥善处理废物。6.4喷涂施工喷涂施工的工艺流程喷涂速凝高分子液体橡胶防水胶膜喷涂施工时应按下列工艺流程施工：机具准备、机具准备、材料准备基层处理交接验收修整自检修整细部施工自检修整喷涂施工成品验收成品养护成品保护层局部加强处理：按设计要求，在结构阴阳角、穿墙管根、施工缝、泛水、落水口等节点、细部构造部位喷涂增强层。增强层采用胎体增强材料时，防水涂料应充分浸透胎体增强材料，不得有露槎。喷涂作业时，喷枪宜垂直于喷涂基层，距离适中，均匀移动。应按照先细部构造后整体喷涂的顺序连续作业，一次多遍、交叉喷涂达到设计要求的厚度。在里面或坡面施工时，喷枪应按照自下而上，由低到高的顺序喷涂，不得漏喷。大面施工时，喷涂施工宜分段分区完成，每个分区以500m2～1000m2为宜。相邻区域喷涂的搭接宽度不应小于100mm。如搭接处有浮浆、灰尘、油污等杂物，应进行清洁处理后可继续喷涂。喷涂速凝高分子液体橡胶防水胶膜喷涂施工完成后，在下道工序施工前，应进行自检，必要时，要进行修补。6.5搭接和甩槎的操作方法平面甩茬：两次喷涂搭接长度不应少于100mm，对30cm的预留部分边缘部位以隔离膜上压砖遮盖进行保护，保护层不能盖过甩槎处。再次喷涂时，先去除隔离膜及砖，喷涂搭接部位并进行后续施工。外防外贴侧墙甩槎：外侧墙喷涂速凝高分子液体橡胶防水胶膜操作顺序应遵循为自下而上操作的原则。喷涂时与立墙紧密粘接，不窜水，不剥离，无需甩茬，不存在像卷材防水层坠落的现象。操作过程中注意铺设起保护层作用的聚苯板不能遮盖已经喷涂的防水胶膜的作业面上端。待回填后，在防水胶膜界面上端继续喷涂（第二次喷涂时，不论间隔多长时间，在原液体橡胶防水层上直接喷涂，不需要做任何处理）。外防内贴时，如侧墙平整，可直接喷涂喷涂速凝高分子液体橡胶防水胶膜。喷涂高度应高于后浇混凝土50cm以上。如侧墙不平整时，可采用悬挂100g无纺布，配置梅花钉的方式，在无纺布上喷涂喷涂速凝高分子液体橡胶防水胶膜，喷涂高度应高于后浇混凝土50cm以上。砖胎膜甩槎：a.在砖胎膜内侧及上部进行喷涂喷涂速凝高分子液体橡胶防水胶膜，按增强层处理；b.在砖胎膜上部加一层隔离膜并压砖对已喷涂的表面上进行保护；c.待浇筑完立墙后，喷涂侧墙防水至砖胎膜上端；d.去除砖胎膜上的砖和隔离膜；e.在砖胎膜和侧墙上喷涂喷涂速凝高分子液体橡胶防水胶膜，使之形成一个整体防水层。6.6保护层施工喷涂速凝高分子液体橡胶防水胶膜施工质量检查验收合格后，应按设计要求及时进行保护层施工。当保护层设计为刚性保护层时，保护层施工不得破坏喷涂速凝高分子液体橡胶防水胶膜。保护层应符合下列规定：1顶板防水层应做细石混凝土保护层，并宜设置分格缝，保护层厚度应符合下列规定：（1）采用机械碾压回填土时，保护层厚度不宜小于70mm；（2）采用人工回填土时，保护层厚度不宜小于50mm；（3）防水层与保护层之间应设置隔离层。2底板防水层宜设置厚度不小于50mm厚的混凝土保护层；3侧墙防水层的保护层宜采用砌体保护，也可采用厚度不宜小于30mm的挤塑聚苯板保护。

7工程验收7.1一般规定喷涂速凝高分子液体橡胶防水胶膜防水层的基面应进行专项验收。喷涂速凝高分子液体橡胶防水胶膜防水层施工完成后应做单项验收。喷涂速凝高分子液体橡胶防水胶膜防水层的最小厚度不得小于设计厚度的90%。喷涂速凝高分子液体橡胶防水胶膜防水层应密实、连续、粘接牢固，无开裂、脱落等缺陷。喷涂速凝高分子液体橡胶防水胶膜防水工程验收时应提交下列资料：1工程防水的设计文件，图纸会审、设计变更、洽商记录单；2产品合格证、质量检验报告、进场抽样复验报告；3施工方案及安全、技术交底文件；4隐蔽工程验收记录；5现场防水渗漏检验记录；6施工记录和施工质量检验记录；喷涂速凝高分子液体橡胶防水胶膜材料进场后进行见证取样复检，复检项目按表7.1.6进行，若材料中有两项或两项以上项目检验结果不符合标准规定，则判定该批材料性能不合格。当材料中仅有一项检验结果不符合标准规定，允许在同批材料中重新取样对该项进行复检，复检结果符合规定时，则判定该批材料物理性能合格，否则判为不合格。进场抽样复检材料，以同一生产时间数量为一个批次为40t。表7.1.6进场抽样复检项目项目指标屋面工程地下工程固体含量/%≥5555耐热度/℃无流淌、滑动、滴落120±290±2不透水性，0.3Mpa120min不透水-胶膜抗渗性，0.3Mpa-120min无渗水断裂伸长率，%≥1000≥800低温柔性-25℃，不断裂-20℃，不断裂检验批次：1屋面工程宜按屋面面积每2000m2划分为一个检验批，不足2000m2应按一个检验批；每1000m2抽查3处；2地下工程宜按屋面面积每10000m2划分为一个检验批，不足10000m2应按一个检验批；每1000m2抽查3处；3厨房、卫生间、水池等以每一个自然间或每一个水池为一个检验批，逐一检验；4其他防水工程参照上述规定。7.2主控项目屋面防水层1屋面防水胶膜应符合设计要求和本规程的规定。检验数量：2000m2检验方法：检查材料出厂合格证、质量检验报告和进场抽样复验报告。2屋面防水层不得有渗漏和积水现象。检验数量：2000m2检验方法：雨后观察或淋水2h、蓄水24h检测。3防水胶膜的平均厚度应符合设计要求和本规程的规定，且最小厚度不得小于设计厚度的90%。检查数量：2000m2。检验方法：采用针测法检测。4防水胶膜在天沟、檐沟、女儿墙、水落口、管根、变形缝、施工缝及后浇带等节点、细部构造防水措施应符合设计要求和本规程的规定。检查数量：单一部位。检验方法：观察检查和检查隐蔽工程验收记录。地下工程防水层1喷涂速凝高分子液体橡胶防水胶膜地下工程防水层应符合设计要求和本规程的规定。检查数量：10000m2。检验方法：检查材料出厂合格证、质量检验报告和进场抽样复验报告。2胶膜防水层的平均厚度应符合设计要求和本规程的规定，且最小厚度不得小于设计厚度的90%。检查数量：10000m2。检验方法：用针测法检查3喷涂速凝高分子液体橡胶在阴阳角、变形缝、施工缝、穿墙管等节点部位做法必须符合设计要求。检查数量：单一部位。检查方法：观察检查和检查隐蔽工程验收记录。7.3一般项目喷涂速凝高分子液体橡胶防水胶膜与基面应粘接牢固，胶膜表面平整、均匀，不得流淌、皱折、翘边缺陷。检查数量：10000m2。检验方法：观察检查。胶膜防水层应连续、无缝隙、无漏喷、无滴落、不流淌。检查数量：10000m2。检验方法：观察检查。防水胶膜的保护层应符合设计要求。检查数量：10000m2。检验方法：观察检查。

8安全和环境保护8.1成品保护喷涂速凝高分子液体橡胶防水胶膜施工时应注意遮挡非工作面，不得污染其他工序及饰面。喷涂速凝高分子液体橡胶防水胶膜施工后不得受重物或尖锐物冲击，不得在已完工的防水层上凿眼打洞，破坏胶膜。喷涂速凝高分子液体