1、 Heat Treatment of Steel 钢的热处理钢的热处理科技英语科技英语n普通热处理普通热处理 normal heat treatment 1.淬火淬火 hardening / quenching 2.回火回火 tempering 3.退火退火 annealingn表面热处理表面热处理 surface heat treatment 1.氰化氰化 cyaniding 2.渗氮渗氮 nitriding 3.渗碳渗碳 carburization Heat Treatment of Steel钢钢 的的 热热 处处 理理Heat treatment is a method by whic

2、h the heat-treater can change the physical properties of a metal. There are three main operations in the heat treatment of steel: hardening, tempering, and annealing.Heat Treatment of Steel钢的热处理钢的热处理译文译文：热处理是热处理是热处理热处理工人工人用来改变金属用来改变金属物理性能的方法。对钢进行热处理可采用三物理性能的方法。对钢进行热处理可采用三种主要的操作：种主要的操作：淬火、回火淬火、回火和和退火

3、退火。heat-treater ：n.热处理工人热处理工人1.1.热处理的含热处理的含 义义 和和 分分 类类harden vi. 淬火淬火temper vi. 回火回火anneal vi. 退火退火The hardening operation consists of heating the steel above its critical range and then quenching it, that is rapidly cooling in a suitable medium such as water, brine , oil, or some other liquid.Heat

4、 Treatment of Steel钢的热处理钢的热处理译文：译文：淬火处理是指将钢材加热到其淬火处理是指将钢材加热到其临界区临界区之上，然后之上，然后降温降温即在适当的介质如水、即在适当的介质如水、盐盐水水、油或其它液体中使之迅速冷却。、油或其它液体中使之迅速冷却。critical range：临界区临界区quench2. 淬淬 火火 hardeningquench：v. 淬火、熄灭淬火、熄灭brine：n.盐水盐水Heat Treatment of Steel钢的热处理钢的热处理consists of 组成，构成，包括，由组成1.The United Kingdom consists o

5、f Great Britain and Northern Ireland. 联合王国包括大不列颠与北爱尔兰。2.His job consists of helping old people who live alone.他的工作包括帮助无人照顾的独居老人。3.Substances consist of small particles called molecules.物质是由叫做分子的微粒组成的。Heat Treatment of Steel钢的热处理钢的热处理Having been hardened , the metal must be given a tempering treatmen

6、t which consists of reheating the hardened steel to a temperature below the critical range, thus producing the required physical properties.临界区以下的某个温度临界区以下的某个温度译文：译文：金属淬硬之后必须进行回火处理，回金属淬硬之后必须进行回火处理，回火是将淬硬的钢重新加热到低于临界区的某火是将淬硬的钢重新加热到低于临界区的某个温度，从而获得所需的物理性能。个温度，从而获得所需的物理性能。3. 回回 火火tempering完成时态表明回火（完成时态表明

7、回火（temper）操作在淬火（操作在淬火（harden）之后）之后。Heat Treatment of Steel钢的热处理钢的热处理一、广泛使用被动语句一、广泛使用被动语句根据英国利兹大学根据英国利兹大学John Swales 的统计，科技英语中的谓语的统计，科技英语中的谓语至少三分之一是被动态。这是因为科技文章侧重叙事推理，至少三分之一是被动态。这是因为科技文章侧重叙事推理，强调客观准确。第一、二人称使用过多，会造成主观臆断强调客观准确。第一、二人称使用过多，会造成主观臆断的印象。因此尽量使用第三人称叙述，采用被动语态，例的印象。因此尽量使用第三人称叙述，采用被动语态，例如：如：Atte

8、ntion must be paid to the working temperature of the machine.应当注意机器的工作温度。而很少说：应当注意机器的工作温度。而很少说：You must pay attention to the working temperature of the machine .你们必须注意机器的工作温度。此外，科技文章你们必须注意机器的工作温度。此外，科技文章将主要信息前置，放在主语部分。这也是广泛使用被动态将主要信息前置，放在主语部分。这也是广泛使用被动态的主要原因。的主要原因。科技英语的特点（一）科技英语的特点（一）Heat Treatment

9、of Steel钢的热处理钢的热处理科技英语的特点（一）科技英语的特点（一）二、后置定语二、后置定语大量使用后置定语也是科技英语的特点之一。常见的结构不外大量使用后置定语也是科技英语的特点之一。常见的结构不外以下五种：以下五种：1、The forces due to friction are called frictional forces.（介词（介词短语）短语）2、In this factory the only fuel available is coal.（形容词及形容（形容词及形容词短语）词短语） 3、The force upward equals the force downwar

10、d so that the balloon stays at the level.（副词）（副词）4、The results obtained must be cheeked.（单个分词），（单个分词），5、During construction, problems often arise which require design changes.（定语从句）（定语从句）在施工过程中，常会出现需要改变设计的问题。在施工过程中，常会出现需要改变设计的问题。Heat Treatment of Steel钢的热处理钢的热处理Annealing is the uniform heating of a

11、metal above usual hardening temperatures, followed by very slow cooling.译文：译文： 退火退火指的是在通常的淬火温度之上将金指的是在通常的淬火温度之上将金属均匀的加热，然后再属均匀的加热，然后再缓慢的冷却缓慢的冷却。4. 退退 火火annealingHeat Treatment of Steel钢的热处理钢的热处理科技英语的特点（一）科技英语的特点（一）三、大量使用名词化结构三、大量使用名词化结构大量使用名词化结构（大量使用名词化结构（Nominalization）是科技英语的特）是科技英语的特点之一。因为科技文体要求行文

12、简洁、表达客观、内容确点之一。因为科技文体要求行文简洁、表达客观、内容确切、信息量大、强调存在的事实。切、信息量大、强调存在的事实。Archimeds first discovered the principle of displacement of water by solid bodies.阿基米德最先发展固体排水的原理。阿基米德最先发展固体排水的原理。科技英语所表述的是客观规律，因之要尽量避免使用第一、科技英语所表述的是客观规律，因之要尽量避免使用第一、二人称；此外，如前所述，要使主要的信息置于句首。二人称；此外，如前所述，要使主要的信息置于句首。Television is the tr

13、ansmission and reception of images of moving objects by radio waves.电视通过无线电波发射和接受活动物体的图象。电视通过无线电波发射和接受活动物体的图象。Annealing may be carried out either to soften a piece that is too hard to machine or to remachine a piece that has already been hardened. Annealing also relieves internal stresses produced b

14、y machining. 重新机加工重新机加工译文：译文： 若工件过硬以致无法机加工，或是要若工件过硬以致无法机加工，或是要重新重新机加工机加工已经淬火变硬的工件，就可通过退火来使材已经淬火变硬的工件，就可通过退火来使材料软化。退火也可以减轻因为机加工而造成的料软化。退火也可以减轻因为机加工而造成的内应内应力。力。内应力内应力4. 退退 火火annealingHeat Treatment of Steel钢的热处理钢的热处理Heat Treatment of Steel钢的热处理钢的热处理5. 表面热处理表面热处理surface heattreatmentLow carbon steel do

15、 not become hard when subjected to such a heat treatment because of the small amount of carbon contained. If it is necessary to obtain a hard surface on a part made of such steel, surface hardening operation must be carried out. 低碳钢低碳钢Low carbon steel表面硬化、表面淬火表面硬化、表面淬火译文：译文： 低碳钢低碳钢因为含碳量少所以在经受这种热处理因为

16、含碳量少所以在经受这种热处理后并不会变硬。如果这种钢材制成的某个零件有必后并不会变硬。如果这种钢材制成的某个零件有必要得到一个较硬的表面，就必须进行要得到一个较硬的表面，就必须进行表面淬火表面淬火处理。处理。cyanide v.氰化氰化Heat Treatment of Steel钢的热处理钢的热处理6. 氰氰 化化cyanidingOne of the methods of surface hardening is cyaniding, which is done by keeping the work in a molten bath of sodium cyanide from 5 to

17、 30 minutes, depending on the size of the work and the depth of penetration required. sodium n. 钠钠 sodium cyanide 氰化钠氰化钠译文：译文： 表面淬火的方法之一是表面淬火的方法之一是氰化氰化，即根据，即根据工件的尺寸和所要求的渗层深度将工件置于工件的尺寸和所要求的渗层深度将工件置于氰化钠熔池氰化钠熔池中保持中保持5 5到到3030分钟。分钟。工件工件（steel）熔池熔池Having been subjected to such a treatment, the work is th

18、en quenched in water or oil,and a very hard case 0.01 to 0.015 inch thick is formed. This process is also called case hardening. Heat Treatment of Steel钢的热处理钢的热处理6. 氰氰 化化cyaniding将工件置于氰化钠将工件置于氰化钠熔池中的氰化处理熔池中的氰化处理表面硬化表面硬化 equals to surface harden 译文：译文： 工件经过这样的处理后被置于水或油工件经过这样的处理后被置于水或油中冷却，就可以形成一中冷却，就可

19、以形成一0.010.01到到0.0150.015英寸厚的英寸厚的硬度层，这一过程也被称为硬度层，这一过程也被称为表面淬火。表面淬火。Heat Treatment of Steel钢的热处理钢的热处理7. 渗渗 氮氮nitridingNitriding is also one of the case hardening methods. This process consists of keeping the steel in hot ammonia gas for some hours. Nitrogen, formed in this condition from ammonia, pene

20、trates into the surface of the metal, thus forming a very hard case.nitride v. 渗氮渗氮ammonia n. 氨、氨水氨、氨水nitrogen n.氮氮译文：译文： 渗氮渗氮也是一种表面淬火方法。其过程为将钢置于热的也是一种表面淬火方法。其过程为将钢置于热的氨蒸气中保持数小时。氨蒸气中保持数小时。氮氮-在该情形下来自于在该情形下来自于氨氨-便会渗入金便会渗入金属表面，形成一非常硬的表层。属表面，形成一非常硬的表层。Heat Treatment of Steel钢的热处理钢的热处理8. 渗渗 碳碳carburizaio

21、nAnother method of the case hardening is carburization. The work is placed into a metal box containing carburizing materials (that is materials with high carbon content)；the box is closed and placed into a furnace for some hours at the temperature of 926 degrees Centigrade. carburization n. 渗碳渗碳摄氏度摄

22、氏度译文：译文： 表面淬火的另一个方法是表面淬火的另一个方法是渗碳渗碳。工件被置于。工件被置于含渗碳材料（即含碳量很高的材料）的金属箱中。封含渗碳材料（即含碳量很高的材料）的金属箱中。封闭箱子将其置于闭箱子将其置于摄氏温度摄氏温度926926的炉膛内数小时。的炉膛内数小时。Heat Treatment of Steel钢的热处理钢的热处理8. 渗渗 碳碳carburizaionThe depth to which the carbon penetrates depends upon the length of time the piece is kept in the furnace. Hav

23、ing been quenched in some liquid quenching medium, the work has a hard case and a soft core.取决于，取决于，= depend on 液体冷却介质液体冷却介质core n.中心，核心，芯部中心，核心，芯部译文：译文：渗碳深度渗碳深度取决于取决于工件在炉膛中保持的时间长度，工件在炉膛中保持的时间长度，经一些经一些液体冷却介质液体冷却介质冷却之后，工件便会形成坚硬的冷却之后，工件便会形成坚硬的表面和较软的表面和较软的芯部芯部。 基本概念基本概念n钢的热处理（钢的热处理（heat treatment of steel）n普通热处理普通热处理 normal heat treatment 1.淬火淬火 hardening/quenching 2.回火回火 tempering 3.退火退火 annealingn表面热处理表面热处理 surface heat treatment 1.氰化氰化 cyaniding 2.渗氮渗氮 nitriding 3.渗碳渗碳 carburizationHeat Treatment of Steel总